Experimental simulation of materials degradation of plasma-facing components using lasers
نویسندگان
چکیده
The damage and erosion of plasma-facing components (PFCs) due to extremely high heat loads and particle bombardment is a key issue for the nuclear fusion community. Currently high current ion and electron beams are used in laboratories for simulating the behaviour of PFC materials under ITER-like conditions. Our results indicate that high-power nanosecond lasers can be used for laboratory simulation of high heat flux PFC material degradation. We exposed tungsten (W) surfaces with repetitive laser pulses from a nanosecond laser with a power density ∼ a few GW cm−2. Emission spectroscopic analysis showed that plasma features at early times followed by intense particle emission at later times. Analysis of laser-exposed W surface demonstrated cracks and grain structures. Our results indicate that the typical particle emission features from laser-irradiated tungsten are consistent with high-power particle beam simulation results.
منابع مشابه
Materials effects and design implications of disruptions and off-normal events in ITER
Damage to plasma-facing components (PFCs) and structural materials during abnormal plasma behavior such as hard disruptions, edge-localized modes (ELMs), and vertical displacement events (VDEs) is considered a serious life-limiting concern for these components. The PFCs in the International Thermonuclear Experimental Reactor (ITER), such as the divertor, limiter and parts of the first wall, wil...
متن کاملImproving the Thermal Characteristics of Semiconductor Lasers Using a New Asymmetric Waveguide Structure
Self-heating leads to a temperature rise of the laser diode and limits the output power and efficiency due to increased loss and decreased differential gain. To control device self-heating, it is required to design the laser structure with a low optical loss, while the heat flux must spread out of the device efficiently. In this study, a new asymmetric waveguide design is proposed and th...
متن کاملPii: S0920-3796(00)00245-3
Surface and structural damage to plasma-facing components (PFCs) due to the frequent loss of plasma confinement remains a serious problem for the tokamak reactor concept. The deposited plasma energy causes significant surface erosion, possible structural failure and frequent plasma contamination. Surface damage consists of vaporization, spallation, and liquid splatter of metallic materials. Str...
متن کاملComprehensive physical models and simulation package for plasma/material interactions during plasma instabilities
Damage to plasma-facing components (PFCs) from plasma instabilities remains a major obstacle to a successful tokamak concept. The extent of the damage depends on the detailed physics of the disrupting plasma, as well as on the physics of plasma-material interactions. A comprehensive computer package called High Energy Interaction with General Heterogeneous Target Systems (HEIGHTS) has been deve...
متن کاملComprehensive Physical Models and Simulation Package for Plasma / Material Interactions during Plasma
Damage to plasma-facing components (PFCS) from plasma instabilities remains a major obstacle to a successful tokamak concept. The extent of the damage depends on the detailed physics of the disrupting plasma, as well as on the physics of plasmamaterial interactions. A comprehensive computer package called B igh Energy interaction with Qeneral Heterogeneous ~arget ~ystems (HEIGHTS) has been deve...