Study on Co-Effect of K2SO4 Deposition and Low Concentration SO2 on Performances of V2O5/AC Catalysts for Low Temperature SCR
نویسندگان
چکیده
Simulated compounds were prepared by loading K2SO4 onto V2O5/AC catalysts. Study the effect of K2SO4 on V1/AC catalysts in the presence of low concentration SO2. Transient response techniques, TPD was carried out. The results indicated that the DeNO activity of V1/AC catalysts was decreased seriously in the early period of operation, but the deactivation was gradually diminished with SO2 adsorption and then, it was completely eliminated. For the sulphated catalysts (saturated catalysts by sulphate), their SCR activity were free from existence of gaseous SO2, the loss of activity about 10% caused by K2SO4 was found on them. The deactivation of K2SO4 deposited catalysts was due to the decrease of adsorbed and activated NH3, or some acid sites.
منابع مشابه
Bauxite-supported Transition Metal Oxides: Promising Low-temperature and SO2-tolerant Catalysts for Selective Catalytic Reduction of NOx
In order to develop low-temperature (below 200 °C) and SO2-tolerant catalysts for selective catalytic reduction (SCR) of NOx, a series of cheap M/bauxite (M = Mn, Ni and Cu) catalysts were prepared using bauxite as a support. Their SCR performances are much superior to typical V2O5/TiO2, the addition of M into bauxite results in significant promotion of NOx removal efficiency, especially at low...
متن کاملLow temperature selective catalytic reduction of NOx with NH3 over Mn-based catalyst: A review
The removals of NOx by catalytic technology at low temperatures (100–300 °C) for industrial flue gas treatment have received increasing attention. However, the development of low temperature catalysts for selective catalytic reduction (SCR) of NOx with ammonia is still a challenge especially in the presence of SO2. The current status of using Mn-based catalysts for low temperature SCR of NOx wi...
متن کاملNH3-SCR performance and the resistance to SO2 for Nb doped vanadium based catalyst at low temperatures.
Niobium oxide as the promoter was doped in the V/WTi catalyst for the selective catalytic reduction (SCR) of NO. The results showed that the addition of Nb2O5 could improve the SCR activity at low temperatures and the 6wt.% additive was an appropriate dosage. The enhanced reaction activity of adsorbed ammonia species and the improved dispersion of vanadium oxide might be the reasons for the ele...
متن کاملSelective Catalytic Reduction of NOx with Methane over Ag-alumina Catalysts in High-content SO2 Gas Streams
In this work, we investigated the performance of Ag-alumina catalysts for the SCR of NO with methane in gas streams with a high concentration of SO2, typical of coal-fired power plant flue gas. Agalumina catalysts were prepared by co-gelation and nitric-acid leaching was used to remove weakly bound silver species from the catalyst surface [1, 2]. We found that SO2 has a dramatic inhibitory effe...
متن کاملSulfur and Water Resistance of Mn-Based Catalysts for Low-Temperature Selective Catalytic Reduction of NOx: A Review
Selective catalytic reduction (SCR) with NH3 is the most efficient and economic flue gas denitrification technology developed to date. Due to its high low-temperature catalytic activity, Mn-based catalysts present a great prospect for application in SCR de-NOx at low temperatures. However, overcoming the poor resistance of Mn-based catalysts to H2O and SO2 poison is still a challenge. This pape...