GeH: a novel material as a visible-light driven photocatalyst for hydrogen evolution.
نویسندگان
چکیده
A novel 2D material germanane (GeH), which was synthesized by an ion-exchange approach, was firstly found to exhibit photocatalytic performance in the hydrogen evolution of water splitting and decomposition of organic contaminants under illumination of visible light (λ ≥ 420 nm).
منابع مشابه
Urchin-like Au@CdS/WO3 micro/nano heterostructure as a visible-light driven photocatalyst for efficient hydrogen generation.
Urchin-like micro/nano heterostructure Au@CdS/WO3 was synthesized by using a facile photodeposition method with no need for an additional stabilizer, which can be used as an efficient all-solid Z-scheme visible-light photocatalyst for H2 generation with a high H2 evolution rate.
متن کاملOrganic-inorganic composite of g-C3N4eSrTiO3:Rh photocatalyst for improved H2 evolution under visible light irradiation
The organic-inorganic composite g-C3N4eSrTiO3:Rh was prepared for the first time as a photocatalyst for hydrogen production and the resulting hydrogen evolution rate under visible light irradiation from aqueous methanol solution was measured. A high hydrogen evolution rate of 223.3 mmol h 1 was achieved by using 0.1 g of as-prepared photocatalyst powder comprised of 20 wt.% g-C3N4 80 wt.% SrTiO...
متن کاملHybridization of Cd0.2Zn0.8S with g-C3N4 nanosheets: a visible-light-driven photocatalyst for H2 evolution from water and degradation of organic pollutants.
Novel visible-light-driven Cd0.2Zn0.8S/g-C3N4 inorganic-organic composite photocatalysts were synthesized by a facile hydrothermal method. The prepared Cd0.2Zn0.8S/g-C3N4 composites were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), high-resolution transmission electron m...
متن کاملA full-sunlight-driven photocatalyst with super long-persistent energy storage ability
A major drawback of traditional photocatalysts like TiO2 is that they can only work under illumination, and the light has to be UV. As a solution for this limitation, visible-light-driven energy storage photocatalysts have been developed in recent years. However, energy storage photocatalysts that are full-sunlight-driven (UV-visible-NIR) and possess long-lasting energy storage ability are lack...
متن کاملSynthesis, Characterization, and Application of Zr,Ce-TiO2/SiO2 Nanocomposite Thin Film as Visible-light Active Photocatalyst
A novel Zr,Ce-TiO2/SiO2 nanocomposite thin film was successfully prepared with various amounts of Zr4+ and Ce4+ as codopant ions for self-cleaning applications. A thin film was coated on a tile substrate by dip-coating and porous Zr,Ce-TiO2/SiO2 was obtained after heat treatment for 2 hours at 500 °C. The SEM images an...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
- Chemical communications
دوره 50 75 شماره
صفحات -
تاریخ انتشار 2014