Electrical and optical properties of Al-doped ZnO and ZnAl2O4 films prepared by atomic layer deposition
نویسندگان
چکیده
ZnO/Al2O3 multilayers were prepared by alternating atomic layer deposition (ALD) at 150°C using diethylzinc, trimethylaluminum, and water. The growth process, crystallinity, and electrical and optical properties of the multilayers were studied with a variety of the cycle ratios of ZnO and Al2O3 sublayers. Transparent conductive Al-doped ZnO films were prepared with the minimum resistivity of 2.4 × 10-3 Ω·cm at a low Al doping concentration of 2.26%. Photoluminescence spectroscopy in conjunction with X-ray diffraction analysis revealed that the thickness of ZnO sublayers plays an important role on the priority for selective crystallization of ZnAl2O4 and ZnO phases during high-temperature annealing ZnO/Al2O3 multilayers. It was found that pure ZnAl2O4 film was synthesized by annealing the specific composite film containing alternative monocycle of ZnO and Al2O3 sublayers, which could only be deposited precisely by utilizing ALD technology.
منابع مشابه
Structure and Electro-Optical Properties of Thin Films Grown by Alternate Atomic Layer Deposition of ZnO and Al_{2}O_{3} on the Sapphire Substrate
Al-doped ZnO thin films were prepared on the (0001) sapphire (c-Al2O3) substrates by atomic layer deposition (ALD) using alternating pulses of Zn(C2H5)2, Al(CH3)3 and H2O precursors and post-deposition high-temperature annealing. Photoluminescence (PL) spectroscopy showed that the threshold of stimulated emission decreases with increasing Al concentration, from 49.2 kW/cm of the ZnO film to 12....
متن کاملEnhanced Physical Properties Of Indium Tin Oxide Films Grown on Zinc Oxide-Coated Substrates
Structural, electrical and optical properties of indium tin oxide or ITO (In2O3:SnO2) thin films on different substrates are investigated. A 100-nm-thick pre-deposited zinc oxide (ZnO) buffer layer is utilized to simultaneously improve the electrical and optical properties of ITO films. High purity ZnO and ITO layers are deposited with a radio frequency sputtering in argon ambient with plasma p...
متن کاملAn experimental and theoretical study on the physical properties of Al doped ZnO thin films
In this research, ZnO thin films with Al impurity as dopant were coated onto cleaned glass substrates by the spray pyrolysis technique. Crystal structure of the thin films was studied via XRD, and UV-vis spectroscopy was carried out to investigate their optical properties. Finally, in order to study the effect of Al impurity in ZnO thin films, the band structures of both pure and doped systems ...
متن کاملCorrelation between crystal structure and optical properties of copper- doped ZnO thin films
ZnO and Cu doped[1] (CZO) thin films were prepared by radio frequency sputtering. The structural and optical properties of thin films were investigated using X-ray diffraction (XRD), atomic force microscopy (AFM), optical spectrophotometer, and photoluminescence (PL) techniques. ZnO thin films showed crystalline and micro-stress defects in the crystal lattice. Annealing of CZO thin films increa...
متن کاملDMMP Sensing Performance of Undoped and Al Doped Nanocrystalline ZnO Thin Films Prepared by Ultrasonic Atomization and Pyrolysis Method
Highly textured undoped (pure) and Al doped ZnO nanocrystalline thin films prepared by ultrasonic atomization and pyrolysis method are reported in this paper. ZnCl2 water solution was converted into fine mist by ultrasonic atomizer (Gapusol 9001 RBI Meylan, France). The mist was pyrolyzed on the glass substrates in horizontal quartz reactor placed in furnace. The Structural and microstructural ...