Grain growth in a bulk nanocrystalline Co alloy during tensile plastic deformation
نویسندگان
چکیده
A bulk nanocrystalline Co–P alloy was subjected to tensile tests. Grain growth from approximately 12 nm in the as-deposited state to about 25 nm after the tensile test was observed. Grain growth was not observed when the deforming volume was increased, or when the specimen was annealed at 433 K or above prior to the tensile tests. 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
منابع مشابه
Abnormal Plastic Behavior of Fine Grain Mp35n Alloy During Room Temperature Tensile Testing
In this paper, results of an investigation on the strain hardening responses of superalloy MP35N with two average grain sizes of 38 and 1 μm, during room temperature tensile testing are reported. The microstructural evolution of the deformed samples was studied using optical and transmission electron microscopy (TEM) techniques. The strain hardening behavior of the 38 μm material was rather sim...
متن کاملNanocrystalline Mg-3%Al Alloy: its Synthesis and Investigation of its Tensile Behavior
The tensile properties of Mg-3%Al nanocrystalline alloys were investigated at different test environment. Bulk nanocrystalline samples of these alloy was successfully prepared by mechanical alloying (MA) followed by cold compaction, sintering, and hot extrusion process. The crystal size of the consolidated milled sample was calculated by X-Ray line profile analysis. The deformation mechanism an...
متن کاملFlow Behavior of SP-700 Titanium Alloy During Hot Tensile Deformation in α+β and β Phase Regions
In this paper, in order to study the flow behavior and elongation of as-cast ingots of SP-700 titanium alloy, hot tensile test was done in α/β dual phase and β single phase regions using strain rate of 0.1 s-1. Results showed that the hot tensile behavior of SP-700 in the α/β dual phase region (700-900 ºC) was different from the β single phase one (950-1100 ºC) due to the nature of alpha and be...
متن کاملThermomechanics of nanocrystalline nickel under high pressure-temperature conditions.
We present a comparative study of thermomechanical properties of nano-polycrystalline nickel (nano-Ni) and micrometer-polycrystalline nickel (micron-Ni) by in situ high pressure-temperature (P-T) diffraction experiments. The yield strength of 2.35 GPa for the nano-Ni measured under high-pressure triaxial compression is more than three times that of the micron-Ni value. Contrary to tensile exper...
متن کاملTensile behavior of Al1 xMox crystalline and amorphous thin films
The exceptional strength and distinct deformation physics exhibited by pure ultrafine-grained and nanocrystalline metals in comparison to their microcrystalline counterparts have been ascribed to the dominant influence of grain boundaries in accommodating plastic flow. Such grain-boundary-mediated mechanisms can be augmented by additional strengthening in nanocrystalline alloys via solute and p...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2006