Analysis of material instability at an impact loaded crack tip
نویسندگان
چکیده
Assuming that a material point becomes unstable when the eective plastic strain there reaches a critical value, it is found that a material instability will initiate at a point on the crack-tip of an impulsively loaded prenotched plate that makes an angle of )14° to the notch-tip. This agrees well with the observed values of )5° to )15°. Ó 1998 Elsevier Science Ltd. All rights reserved.
منابع مشابه
On the mechanics of fracture in monoliths and multilayers from low-velocity impact by sharp or blunt-tip projectiles
The propagation of cracks in layered glass from low-velocity impact of sharp or spherical tip projectiles is observed using high-speed photography. Tests are also carried out to determine the threshold impact energy for chipping in glass blocks and subsurface crack instability in an edge-supported glass plates. The results identify the median and subsurface radial crack systems as the prime dam...
متن کاملSimulation of brittle and ductile fracture in an impact loaded prenotched plate
We analyze the initiation and propagation of a crack from a point on the surface of a circular notch-tip in an impact loaded prenotched plate. The material of the plate is assumed to exhibit strain hardening, strain-rate hardening, and softening due to the rise in temperature and porosity. The degradation of material parameters due to the evolution of damage in the form of porosity is considere...
متن کاملViscoelastic Strip
Associate Professor, Graduate Aeronautical laboratories, California Institute of Technology, Pasadena, Calif. The tip velocity of a crack propagating through a vi scoelastic material depends on geometry, apptied toad and its history , and material properties. A consideration of the work done by the unloading tractions at the crack tip shows that, f or a large crack propagating throitgh an infin...
متن کاملThe e'ect of crack blunting on the competition between dislocation nucleation and cleavage
To better understand the ductile versus brittle fracture behavior of crystalline materials, attention should be directed towards physically realistic crack geometries. Currently, continuum models of ductile versus brittle behavior are typically based on the analysis of a pre-existing sharp crack in order to use analytical solutions for the stress 8elds around the crack tip. This paper examines ...
متن کاملEffect of Crack Geometry on Dislocation Nucleation and Cleavage Thresholds
A continuum model based upon the Peierls-Nabarro description of a dislocation ahead of a crack is used to evaluate the critical mode I loading for dislocation nucleation at the tip of a finite, pre-blunted crack. A similar approach is used to evaluate the critical mode I loading for atomic decohesion. Results are presented for various crack tip root radii (a measure of bluntness), for several c...