Synthesis and electrochemical properties of niobium pentoxide deposited on layered carbide-derived carbon
نویسندگان
چکیده
Nb2O5 nanoparticles were hydrothermally deposited on carbidederived carbon (CDC). Addition of phenylphosphonic acid affects the particle size and
منابع مشابه
Electrochemical Energy Storage Applications of CVD Grown Niobium Oxide Thin Films.
We report here on the controlled synthesis, characterization, and electrochemical properties of different polymorphs of niobium pentoxide grown by CVD of new single-source precursors. Nb2O5 films deposited at different temperatures showed systematic phase evolution from low-temperature tetragonal (TT-Nb2O5, T-Nb2O5) to high temperature monoclinic modifications (H-Nb2O5). Optimization of the pre...
متن کاملSynthesis of calcium carbide-derived carbon by mechanochemical reaction of calcium carbide with sulfur, iron sulfide and zinc oxide
In the present work, we report a novel design and preparation for the mechanochemical synthesis of calcium carbide-derived carbon (CaC2-CDC) at ambient temperature. Thermodynamic calculations confirmed the possibility of calcium carbide-derived carbon formation by the reaction of calcium carbide with sulfur, iron sulfide and zinc oxide at ambient temperature. The CDCs were synthesized by the ba...
متن کاملFabrication and Characterization of Polymer Blend Doped With Metal Carbide Nanoparticles for Humidity Sensors
Nanocomposites films of (polymer blend-ceramics) were prepared from (PVA-PAA) blend and (PVA-PAA) blend doped with niobium carbide nanoparticles for humidity sensors have low cost, easy fabrication, high sensitivity, lightweight and high corrosion resistance. The structural, electrical and optical properties of (PVA-PAA-NbC) nanocomposites have been studied. The D.C electrical properties of (PV...
متن کاملSTUDY ON NIOBIUM CARBIDE COATING FORMATION ON AISI L2 STEEL USING THERMO-REACTIVE DEPOSITION METHOD
In the present research, to form niobium carbide coating on the surface of AISI L2 steel Thermo-Reactive Deposition method (TRD) in a molten bath was used. Niobium carbide coating treatment was carried out at 1173 K, 1273 K, and 1373 K for 2, 4, and 8 hours. The molten bath contained 20wt.% borax (Na2B4O7), 5 wt.% boric acid (B2O3), and 75 wt.% ferro-niobium. The presence and properties of...
متن کاملKinetic Study of Niobium Carbide Coating Formation on AISI L2 Steel using Thermo-Reactive Deposition Technique
In the present study, Thermo-Reactive Deposition method (TRD) in a molten bath was used to form niobium carbide coating on AISI L2 steel. The coating was formed in five different composition of borax (Na2B4O7), boric acid (B2O3), and ferro-niobium. For all of the five compositions of molten bath, niobium carbide coating treatment was carried out at 1173 K, 1273 K, and 1373 K for 2, 4 and 8 hour...