Improvement of vibrodamping properties of polyvinyl acetate–graphite composites by electron beam processing of the filler
نویسندگان
چکیده
The effect of electron beam processing (energy 900 keV, absorbed dose in the range from 25 to 600 kGy) of graphite upon the efficiency of its use as a filler in polyvinyl acetate (PVA) based vibrodamping composites is studied. Graphite treatment at optimal doses above 200 kGy is found to provide a significant increase of damping loss factor for these composites at ambient and especially at elevated temperatures. The observed improvement of vibrodamping properties correlates with the increase in the content of Broensted centers (hydroxyl groups) on modified graphite surface probably due to the additional bonding of the filler particles with each other and PVA binder.
منابع مشابه
Electrical properties of UHMWPE/graphite nanoplates composites obtained by in-situ polymerization method
There are described nanocomposites based on ultra high molecular weight polyethylene and graphite nanoplates prepared by in-situ polymerization method. It is carried out a comprehensive study of electric properties of these composites, including direct current (dc) and alternating current (ac) properties. There is explored dependence of the conductivity and dielectric permeability on filler con...
متن کاملEffect of Silicon Carbide and graphite additives on the pressureless Sintering mechanism and microstructural characteristics of Ultra-High Temperature ZrB2 Ceramics Composites
The effect of SiC content, additives, and process parameters on densification and microstructural properties of pressureless sintered ZrB2– (1–10 wt %) SiC particulate composites have been studied. The ZrB2–SiC composite powders mixed by Spex mixer with 1-2wt% C (added as graphite powder) and CMC have been cold-compacted and sintered in argon environment in the temperature range of 1800–2100ºC ...
متن کاملCorrelation between Mechanical Properties with Specific Wear Rate and the Coefficient of Friction of Graphite/Epoxy Composites
The correlation between the mechanical properties of Fillers/Epoxy composites and their tribological behavior was investigated. Tensile, hardness, wear, and friction tests were conducted for Neat Epoxy (NE), Graphite/Epoxy composites (GE), and Data Palm Fiber/Epoxy with or without Graphite composites (GFE and FE). The correlation was made between the tensile strength, the modulus of elasticity,...
متن کاملIntroducing a novel Polyvinyl chloride/Tungsten composites for shielding against gamma and X-ray radiations
Introduction: This study introduces a novel polyvinyl chloride (PVC)/tungsten composites with characterization of their shielding properties by employing different techniques. Methods: The PVC/tungsten composites were produced by employing various weight fractions of tungsten micro-particles including 0, 20, and 40 % wt via melt blending method. In the next st...
متن کاملFabrication of Al/Graphite/Al2O3 Surface Hybrid Nano Composite by Friction Stir Processing and Investigating The Wear and Microstructural Properties of The Composite
Friction stir processing was applied for fabricating an aluminum alloy based hybrid nano composite reinforced with nano sized Al2O3 and micro sized graphite particles. A mixture of Al2O3 and graphite particles was packed into a groove with 1 mm width and 4.5 mm depth, which had been cut in 5083 aluminum plate of 10 mm thick. Packed groove was subjected to friction stir processing in order to im...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره 5 شماره
صفحات -
تاریخ انتشار 2016