Mechanical behaviour of a new automotive high manganese TWIP steel in the presence of liquid zinc

iii Abstract: High manganese TWIP (TWinning Induced Plasticity) steels are particularly attractive for automotive applications because of their exceptional properties of strength combined with an excellent ductility. However, as austenitic steels, they appear to be sensitive to liquid zinc embrittlement during welding, the liquid zinc arising from the melted coating due to the high temperatures reached during the welding process. In this framework, the cracking behaviour of a high manganese austenitic steel has been investigated in relation to the liquid metal embrittlement (LME) phenomenon by hot tensile tests carried out on electro-galvanized specimens using a Gleeble 3500 thermomechanical simulator. The influence of different parameters such as temperature and strain rate on cracking behaviour has been studied. Embrittlement appears within a limited range of temperature depending on experimental conditions. Conditions for which cracking occurs could be experienced during welding processes. The existence of a critical stress above which cracking appears has been evidenced and this critical stress can be used as a cracking criterion. Finally, the study of the influence of different parameters such as time of contact between steel and liquid zinc before stress application, coating and steel on LME occurrence provides understanding elements of LME mechanism and permits to suggest solutions for preventing cracking during spot welding of such steels.