Effect of TEOS Electrospun Nanofiber Modified Resin on Interlaminar Shear Strength of Glass Fiber/Epoxy Composite
ثبت نشده
چکیده
Interlaminar shear strength (ILSS) of fiber reinforced polymer composite is an important property for most of the structural applications. Matrix modification is an effective method used to improve the interlaminar shear strength of composite. In this paper, EPON 862/w epoxy system was modified using Tetraethyl orthosilicate (TEOS) electrospun nanofibers (ENFs) which were produced using electrospinning method. Unmodified and nanofibers modified resins were used to fabricate glass fiber reinforced polymer composite (GFRP) using H-VARTM method. The ILSS of the Glass Fiber Reinforced Polymeric Composites (GFRP) was investigated. The study shows that introduction of TEOS ENFs in the epoxy resin enhanced the ILSS of GFRPby 15% with 0.6% wt. fraction of TEOS ENFs. Keywords—Electrospun nanofibers, H-VARTM, Interlaminar shear strength (ILSS), Matrix modification.
منابع مشابه
Toughening of a Carbon-Fibre Composite Using Electrospun Poly(Hydroxyether of Bisphenol A) Nanofibrous Membranes Through Inverse Phase Separation and Inter-Domain Etherification
The interlaminar toughening of a carbon fibre reinforced composite by interleaving a thin layer (~20 microns) of poly(hydroxyether of bisphenol A) (phenoxy) nanofibres was explored in this work. Nanofibres, free of defect and averaging several hundred nanometres, were produced by electrospinning directly onto a pre-impregnated carbon fibre material (Toray G83C) at various concentrations between...
متن کامل(افزایش مقاومت خمشی کامپوزیتها توسط کشش الیاف (یادداشت فنی
In the present research work, the flexural modulus and strength of glass fiber-epoxy resin and carbon fiber-epoxy resin composites have been enhanced through fiber tension during curing of the polymeric resin. This study showed that the tension applied on the fibers increased the flexural modulus of the glass-epoxy composites up to 12% and the flexural strength up to 19%. The flexural modulus a...
متن کاملRelationship of Interface Fracture Energy and Interlaminar Shear Strength of Carbon Fiber Reinforced Composite under Hydrothermal Treatment
The mechanical and physical properties of composite materials are greatly influenced by the structure and properties of fiber/matrix interface. Short beam shear test is often performed to evaluate the laminar interface properties in real applications, especially for studying them after a given hydrothermal treatment. However, the results depend on the interface and the matrix properties, so the...
متن کاملCharacterization of Nanocomposite Laminates Fabricated from Aqueous Dispersion of Nanoclay
Preparation of E-glass/waterborne epoxy prepregs containing natural nanoclay and properties of their composites are presented. Prepregs were prepared by wetting randomly oriented, chopped glass fiber preforms with aqueous dispersion of EpiRez 3522-W-60 resin, dicyandiamide, 2-methylimidazole and natural nanoclay (Cloisite Naþ). The nanoclay content of the aqueous dispersion was adjusted to yiel...
متن کاملEffect of Epoxy Functional Groups on the Properties of Carbon Fiber-Epoxy Composites
Matrix resins of carbon fiber-epoxy composites with different numbers of epoxy functional groups were prepared, and their properties were compared to optimize the matrix resin composition. To understand the bonding strengths between the carbon fiber and epoxy resins in monofilaments and micro-sized resin beads, the interfacial shear strength (IFSS) was measured using the microdroplet technique....
متن کامل