In Vitro Cytotoxicity and Setting Time Assessment of Calcium-Enriched Mixture Cement, Retro Mineral Trioxide Aggregate and Mineral Trioxide Aggregate

Introduction The present study sought to evaluate and compare biocompatibility and setting time of Retro mineral trioxide aggregate (MTA), calcium-enriched mixture (CEM) and Angelus MTA. Methods and Materials CEM cement, Angelus MTA and Retro MTA were assessed in set and fresh states. Extracts transformed to each cavity of three 24-well plates in which 1×104 cell were seeded into each well 24 h earlier. All specimens were incubated in a humidified incubator with 5% CO2 at 37°C. Mosmann's tetrazolium toxicity (MTT) assay was used to determine in vitro cytotoxicity on L929 mouse fibroblast cell line. Cell viability was determined at 1, 24, and 72 h after exposure. The initial setting time was measured by 113.4 g Gilmore needle testing. Then, final setting times were assessed by the 456.5 g Gilmore needle. Data comparisons were performed using the analysis of variance (ANOVA) and Tukey's post hoc test (α=0.05). Results All groups in both forms indicated higher cell vitality compared to positive control group (P<0.001). After 24 h, the set Retro MTA showed better biocompatibility compared to set CEM and set Angelus MTA (P<0.001). Retro MTA showed significantly lower initial and final setting time compared to CEM and Angelus MTA (P<0.001). Conclusion Our results indicated the good cell viability values of Retro MTA and relatively short period of setting time. It seems a promising alternative material in clinical situations where accelerated setting is required. However, more clinical and in vivo investigations are needed for a clear decision making.