In situ synthesis of flexible magnetic γ-Fe2O3@SiO2 nanofibrous membranes.
نویسندگان
چکیده
Novel flexible, mesoporous, and magnetic γ-Fe2O3@SiO2 nanofibrous membranes with high γ-Fe2O3 content and uniform distribution were prepared by a facile in situ growth method, which exhibit prominent mechanical strength and magnetic responsive performance, as well as efficient adsorption for organics in water.
منابع مشابه
Synthesis and Characterization of SiO2 Coated γ-Fe2O3 Nanocomposite Powder for Hyperthermic Application
SiO2 coated γ-Fe2O3 nanocomposite powder has been successfully synthesized by chemical vapor condensation process and its feasibility on hyperthermic application was investigated in this study. The power loss of SiO2 coated γ-Fe2O3 nanocomposite powder which means the magnetic heating effect under alternative magnetic field was much higher than the single phase γ-Fe2O3 nano powder due to the ve...
متن کاملDouble-faced γ-Fe2O3||SiO2 nanohybrids: flame synthesis, in situ selective modification and highly interfacial activity.
Double-faced γ-Fe2O3||SiO2 nanohybrids (NHs) and their in situ selective modification on silica faces with the 3-methacryloxypropyltrimethoxysilane molecules have been successfully prepared by a simple, rapid and scalable flame aerosol route. The double-faced NHs perfectly integrate magnetic hematite hemispheres and non-magnetic silica parts into an almost intact nanoparticle as a result of pha...
متن کاملA general strategy for fabricating flexible magnetic silica nanofibrous membranes with multifunctionality.
Flexible, magnetic, and hierarchical porous NiFe2O4@SiO2 nanofibrous membranes were prepared by combining the gelatin method with electrospun nanofibers. The membranes exhibited prominent mechanical strength and mesoporosity, as well as multifunctionality of magnetic responsiveness, dye adsorption, and emulsion separation.
متن کاملSono-synthesis of Novel Magnetic Nanocomposite (Ba-α-Bi2O3-γ-Fe2O3) for the Solar Mineralization of Amoxicillin in an Aqueous Solution
In this study, a novel magnetic nanocomposite (Ba-α-Bi2O3-γ-Fe2O3) was successfully synthesized through a combination of ultrasound and co-precipitation method under mild conditions. The structure of the synthesized nano-composite as a visible light photocatalyst was investigated by the XRD, TEM, HRTEM, UV-vis and FT-IR. The HRTEM confirmed that the nano-magnetic composites are rods with diamet...
متن کاملSynthesis and characterization of magnetic γ- Fe2O3 nanoparticles: Thermal cooling enhancement in a sinusoidal headbox
Nano-size maghemite (γ-Fe2O3) particles were prepared in one step using ultrasound radiation. The obtained nanoparticles were characterized by SEM, TEM , XRD, FTIR, and VSM. The results revealed that the synthesized nanoparticles were spherical, mono-dispersed and uniform. Furthermore, the crystalline structure of nanoparticles endorsed by X-ray diffraction study. The FTIR spectra have provided...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Nanoscale
دوره 6 4 شماره
صفحات -
تاریخ انتشار 2014