Corrosion Behavior of a Fe-25at%Sn Supersaturated Solid Solution in H3PO4 Solution
Corrosion resistance of iron can be drastically improved by addition of passivating alloying elements. A supersaturated solid solution of Fe-25at%Sn was produced by mechanical alloying of commercially pure iron and tin powders for 24 hours using a planetary ball mill. Electrochemical measurements were performed on cold compacted unsintered specimens.. XRD investigation on produced alloy showed ...
متن کاملSolubility Study in Ag-Cu Binary System Prepared By Ball Milling Process
Solid solutions of Ag-Cu were prepared via ball milling process, for about 5-30 h. The Cu-20at%Ag and Cu-3.64at%Ag composition were investigated by X-ray diffraction technique. It was realized that the solid solubility level could be increased by increasing the initial solute content in the mixture. In addition, shifts in peak positions of silver and copper were observed with milling time. The ...
متن کاملCharacterization of the metastable Cu-Fe nanoparticles prepared by the mechanical alloying route
Although Cu and Fe are immiscible under equilibrium conditions, they can form supersaturated solid solutions by mechanical alloying. In this paper, nano-structured of the metastable Cu-Fe phase containing 10, 15, 20 and 25% wt Fe were synthesized by intensive ball milling for 15h, in order to achieve a solid solution of Fe in Cu. The phase composition, dissolution of the Fe atoms into the Cu ma...
متن کاملEffect of Combination on Properties of Cu-Ag Nanocomposites Synthesized by Heat Treatment
Ag-Cu solid solutions prepared via ball milling process were subsequently milled for 30 h and investigated by X-ray diffraction technique for Cu-20%Ag, Cu-3.64%Ag and Cu-80%Ag. It was noted that the solid solubility level increased by increasing initial solute content in composition. Results showed peak positions of silver and copper changed with milling time. By heating up to 700 K, ...
متن کاملProduction of Fe-TiN and Fe-Ti(N,C) composite powders by mechanical alloying
In this research, the production of Fe-TiN and Fe-Ti(N,C) composite powders by mechanical alloying was investigated and evaluated. Ferrotitanium (containing 70%Ti), titanium and graphite were used as the raw materials. Initial mixtures were milled in different time durations under the pure nitrogen atmosphere with the pressure of 5atm. The results showed that when N2 pressure is 5 at...