جوابهای خودسازگار ساختار الکترونی PrBa2Cu3O7 با LSDA+U
نویسندگان
چکیده مقاله:
Based on the density functional theory and using the full-potential linearized augmented-plane-waves method the electronic structure of PrBa2Cu3O7 (Pr123) system was calculated. The rotationally invariant local spin density approximation plus Hubbard parameter U was employed for Pr(4f) orbitals. One self-consistent solution more stable than the previous solution, which has been proposed by Liechtenstein and Mazin (LM), was found. In contrast to the LM solution, it can explain the results of the 17O NMR spectroscopy study of nonsuperconducting Pr123 samples. This new solution favors the suggestion that the pure Pr123 samples should be intrinsically superconductor and metal similar to the other RBa2Cu3O7 (R=Y or a rare earth element) samples. The imperfections cause the superconducting holes are transferred to the nonsuperconducting hole states around the high-symmetry (π/a, π/b, kz) line in the Brillouin zone and so, superconductivity is suppressed in the conventional samples. It predicts that the superconducting 2pσ holes in the O2 sites of nonsuperconducting Pr123 samples should be depleted and the ones in the O3 sites should be almost unchanged .
منابع مشابه
جوابهای خودسازگار ساختار الکترونی prba۲cu۳o۷ با lsda+u
براساس نظریه تابعی چگالی و با روش امواج تخت بهبودیافته در تقریب lsda+u ، ساختار الکترونی prba2cu3o7 محاسبه شد. یک جواب خودسازگار دیگر علاوه بر آنچه قبلاً ارائه شده بود به دست آمد (نظریه lm ). بر خلاف جوابهای lm این حل خودسازگار قابلیت توجیه نتایج nmr نمونه غیر ابررسانای prba2cu3o7 را دارد. این حل خودسازگار جدید پیشنهاد می کند که 123 pr خالص و بدون هیچ نقصی باید ذاتاً ابررسانا باشد. ناکاملیهای ش...
متن کاملمطالعه ساختاری و الکترونی geh4 تحت فشار با رویکرد خودسازگار
هیدروژن فلزی ، سبکترین عنصر جدول تناوبی ، بدلیل ویژگیهای عجیب و کاربردهای مهم همواره مورد توجه دانشمندان نظری و تجربی بوده است. اما با وجود آزمایشهای فشار زیادی که انجام شده است ، تاکنون هیچ اثری از گذار به حالت فلزی هیدروژن به دست نیامده است. هیدرایدهای گروه 4 جدول تناوبی (ch4 , sih4 , geh4 , snh4) تحت فشار بسیار کمتری نسبت به هیدروژن فلزی می شوند . عناصر این گروه بدلیل داشتن ساختار الماسی و س...
15 صفحه اولتعیین ساختار تک بلور های CdTe با میکروسکوپ الکترونی تراگلیسی
Single crystals of CdTe were grown by the sublimation and condensation technique in a silica, under an argon gas now, and also by alloing cadmium tcJloride transport within an evacuated silica ampoule. X-ray powder diffraction patlerns prepared from each group of grown crys tals showed the crystal structure of the examined samples to be zinc-blend race-cent red cubic. Transmission electr...
متن کاملSuppression and restoration of superconductivity in PrBa2Cu3O7
One of the most exciting cases of superconductivity suppression in high-Tc cuprates is that of RE1−xPrxBa2Cu3O7, where RE stands for a rare earth (see Refs. [1,2] for reviews). Even more exciting are indications that conductivity and superconductivity can be restored in stoichiometric PrBa2Cu3O7 [3,4]. This is such an unexpected result [5] that it is still not generally accepted and further exp...
متن کاملمطالعۀ ویژگیهای ساختار الکترونی ابررسانای Nb3Ga
در این مقاله ساختار نواری، چگالی حالت‌ها و چگالی ابر الکترونی ترکیب Nb3Ga در فاز مکعبی مورد بررسی قرار گرفته است. محاسبات با استفاده از روش امواج تخت خود سازگار ( PWscf ) در چارچوب نظریۀ تابعی چگالی توسّط بستۀ نرمافزاری Espresso انجام شده است و نتایج به دست‌آمده سازگاری خوبی با نتایج دیگر محاسبات دارد.
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ذخیره در منابع من قبلا به منابع من ذحیره شده{@ msg_add @}
عنوان ژورنال
دوره 9 شماره 1
صفحات 99- 103
تاریخ انتشار 2009-08
با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.
کلمات کلیدی برای این مقاله ارائه نشده است
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023