A Tri-modal 2024 Al -B4C composites with super-high strength and ductility: Effect of coarse-grained aluminum fraction on mechanical behavior

نویسندگان

  • Ali Alizadeh Faculty of Materials & Manufacturing Processes, Malek-e-Ashtar University of Technology, Tehran, Iran.
  • Alireza Abdollahi Faculty of Materials & Manufacturing Processes, Malek-e-Ashtar University of Technology, Tehran, Iran.
چکیده مقاله:

In this study, ultrafine grained 2024 Al alloy based B4C particles reinforced composite was produced by mechanical milling and hot extrusion. Mechanical milling was used to synthesize the nanostructured Al2024 in attrition mill under argon atmosphere up to 50h. A similar process was used to produce Al2024-5%wt. B4C composite powder. To produce trimodal composites, milled powders were combined with coarse grained aluminum in 30 and 50 wt% and then were exposed to hot extrusion at 570°C. The microstructure of hot extruded samples were studied by optical microscope, Transmission electron microscope (TEM) and scanning electron microscope (SEM) equipped with EDS spectroscopy. The mechanical properties of samples were compared by using tensile, compression and hardness tests. The results showed that the strength, after 50 h milling and addition of 5wt% B4C, increased from 340 to 582 MPa and the hardness increased from 87 HBN to 173 HBN, but the elongation decreased from 14 to 0.5%. By adding the coarse-grained aluminum powder, the strength and hardness decreased slightly, but the increases in return. Ductility increase is the result of increase in dislocation movements and strength increase is the result of restriction in plastic deformation by nanostructured regions. Furthermore, the strength and hardness of trimodal composites were higher, but their ductility was lower.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

a tri-modal 2024 al -b4c composites with super-high strength and ductility: effect of coarse-grained aluminum fraction on mechanical behavior

in this study, ultrafine grained 2024 al alloy based b4c particles reinforced composite was produced by mechanical milling and hot extrusion. mechanical milling was used to synthesize the nanostructured al2024 in attrition mill under argon atmosphere up to 50h. a similar process was used to produce al2024-5%wt. b4c composite powder. to produce trimodal composites, milled powders were combined w...

متن کامل

Mechanical behavior of ultrafine-grained Al composites reinforced with B4C nanoparticles

The influence of nanoscale reinforcement on the mechanical behavior of ultrafine-grained composites was studied. Al 5083 (Al– 4.5 Mg–0.57Mn–0.25Fe) composites, with grain size of 115 nm and B4C reinforcement size of 38 nm, were fabricated via cryomilling and consolidation. The result reveals that the presence of nanoparticles enhances strength by interacting with dislocations, while simultaneou...

متن کامل

Study on the strengthening mechanisms and failure modes of the ultra-fine grained tri-modal Al5083-5wt. %B4C-Al2024 and Al5083-5 wt. %B4C-Al5083 composites

In this paper, the influence of Al2024 and Al5083 aluminum alloy coarse grains on mechanical properties and fracture mechanism of Al5083-B4C tri-modal composite has been discussed. Al5083 alloy powders with 5 wt. % of boron carbide were milled for 36 hours and 25 and 50 wt. % of coarse grain (CG) Al2024 and Al5083 powders were added to the milled powders and then hot press under argon atmospher...

متن کامل

Towards electroformed nanostructured aluminum alloys with high strength and ductility

Towards electroformed nanostructured aluminum alloys with high strength and ductility. Article is made available in accordance with the publisher's policy and may be subject to US copyright law. Please refer to the publisher's site for terms of use. The MIT Faculty has made this article openly available. Please share how this access benefits you. Your story matters. Nanostructured Al–Mn alloys ...

متن کامل

Effect of Temperature and Aging Time on 2024 Aluminum Behavior

This study is a follow-up of previous work by the authors on the effects of processing variables on the deformation and fracture of 2024-T4 aluminum. In the previous work, four variables were incorporated into a Design of Experiments methodology: solution temperature, solution time, cooling rate and natural aging time. Solution time and cooling rate were found to be the most significant factors...

متن کامل

Mechanical and Tribological Behavior of Aluminum Alloy LM13 Reinforced with Titanium Dioxide Metal Matrix Composites

In the present research work physical, mechanical and tribological behavior of Aluminum (Al) alloy LM13 reinforced with Nano-sized Titanium Dioxide (TiO2) particulates were fabricated, mechanical and tribological properties were investigated. The amount of nano TiO2 particulates in the composite was added from 0.5% to 2% in 0.5 weight percent (wt %) increments. The Al-LM13-TiO2 Metal Matrix Com...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 47  شماره 2

صفحات  77- 88

تاریخ انتشار 2014-12-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023