Control Of C/Ti Ratio in Titanium Carbide - Copper Master Alloys Produced by SHS Reactions and its Effect on the Carbide Dispersion In Liquid Copper

نویسنده

  • N. Zarrinfar and A. Saidi
چکیده مقاله:

Titanium carbide is used as an attractive reinforcement to produce particulate metal matrix composites. One of the problems to use this carbide as a reinforcement in copper-based composites is the lack of wetability in Cu-TiC system. This property improves as the C/Ti ratio in carbide decreases.&#10Problems to use this carbide as a reinforcement in copper-based composites is the lack of wetabiity in Cu-TiC system. This property improves as the C/Ti ratio in carbide decreases.&#10A practical method is presented in this paper to improve the dispersion of titanium carbide into liquid copper and emphasis is placed on the C/Ti ratio in the carbide. It was observed that the C/Ti ratio in a raw mixture containing only Ti and C was equal to C/Ti ratio in the carbide after synthesis but when copper powder was added to the raw materials, this ratio was higher than the starting value. Regarding the relationship between the titanium carbide lattice parameter and the C/Ti ratio in the carbide and this ratio in the raw mixture, a graph was drawn that related the C/Ti=1, a network of agglomerated TiC particles with the same C/Ti ratio is formed which cannot be dispersed into liquid copper. When this ratio is decreased to 0.3, particulate titanium carbide with C/Ti=0.5 can be easily dispersed into liquid copper.&#10&#10Keywords: SHS reaction, titanium carbide&#10

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Development of Creep-Resistant Tungsten Carbide Copper Cemented Carbide

Fine-grained tungsten carbide copper (WC-Cu) cemented carbide was sintered via spark plasma sintering at 1773K using a fine WC powder with a mean particle size of 0.11 mm. The mechanical properties were compared with tungsten carbide cobalt (WC-Co) cemented carbide and a binderless WC-sintered material. The Vickers hardness and fracture toughness obtained by the indentation fracture method for ...

متن کامل

the washback effect of discretepoint vs. integrative tests on the retention of content in knowledge tests

در این پایان نامه تاثیر دو نوع تست جزیی نگر و کلی نگر بر به یادسپاری محتوا ارزیابی شده که نتایج نشان دهندهکارایی تستهای کلی نگر بیشتر از سایر آزمونها است

15 صفحه اول

the effect of oxytetracycline on serum calcium, phosphorus and magnesium in cattle

نتایج این مطالعه نشان می دهد که مقدار کلسیم (یونیزه و تام)، منیزیم و فسفر به طور معنی داری تغییر پیدا کرد به جزء مقدار کلسیم تام و منیزیم در روش داخل عضلانی که تغییر معنی داری نداشته است. بر اساس نتایج این مطالعه می توان نتیجه گیری کرد که اکسی تتراساکلین بر روی مقادیر سرمی کلسیم و منیزیم تأثیر می گذارد باید مقدار این کاتیون ها در بیماران، در هنگامی که اکسی تتراسایکلین استفاده می شود مورد توجه ق...

15 صفحه اول

the effect of e-64 on the developmental competence of sheep cocs during in vitro maturation

in the present study, the effect of e-64 at different concentrations (0.5, 1, 5 and 10 µm) added to (1) the ivm medium on oocyte nuclear maturation and developmental competence of ovine oocytes, and (2) to the ivc medium on embryonic development of ovine embryos were investigated.

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 21  شماره 2

صفحات  125- 132

تاریخ انتشار 2003-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

کلمات کلیدی

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023