Effect of Alumina Addition to Zirconia Nano-composite on Low Temperature Degradation Process and Biaxial Strength

نویسندگان

  • Batoul Hashemibeni Department of Anatomical Sciences and Molecular Biology, School of Medicine, Isfahan University of Medical Sciences, Isfahan 81746-73461, Iran.
  • Farahnaz Nejatidanesh Dental Materials Research Center, School of Dentistry, Isfahan University of Medical Sciences, Isfahan,Iran.
  • Mohammadhossein Fathi Biomaterials Reserach Group, Department of Materials Engineering, Isfahan University of Technology, Isfahan, 84156-83111, Iran.|Dental Materials Research Center, School of Dentistry, Isfahan University of Medical Sciences, Isfahan,Iran.
  • Moluk Aivazi Biomaterials Reserach Group, Department of Materials Engineering, Isfahan University of Technology, Isfahan, 84156-83111, Iran.
  • Vajihesadat Mortazavi Torabinejad Dental Research Center, Department of Operative Dentistry, School of Dentistry, Isfahan University of Medical Sciences, Isfahan 81746-73461, Iran.
چکیده مقاله:

Ceramic dental materials have been considered as alternatives to metals for dental implants application. In this respect, zirconia tetragonal stabilized with %3 yttrium, is of great importance among the ceramic materials for endosseous dental implant application. Because of its good mechanical properties and color similar to tooth. The aim and novelty of this study was to design and prepare Y-TZP nano-composite to reduce the degradation process at low temperature by alumina addition and maintaining submicron grain sized. Also, flexural strength of nano-composite samples was evaluated. Toward this purpose, alumina-Y-TZP nano-composites containing 0–30 vol% alumina (denoted as A-Y-TZP 0-30) were fabricated using α-alumina and Y-TZP nano-sized by sintering pressure less method. The synthesized samples were characterized using x-ray diffraction, field emission scanning electron microscopy equipped with energy dispersive x-ray spectroscopy techniques. Nano-composite samples with high density (≥96%) and grain sized of ≤ 400 nm was obtained by sintering at 1270 °C for 170 min. After low temperature degradation test (LTD), A-Y-TZP20 and A-Y-TZP30 not showed monoclinic phase and the flexural strength in all of samples were higher than A-Y-TZP0. It was concluded that the grains were remained in submicron sized and A-Y-TZP20 and A-Y-TZP30 did not present biaxial strength reduction after LTD test.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

effect of alumina addition to zirconia nano-composite on low temperature degradation process and biaxial strength

ceramic dental materials have been considered as alternatives to metals for dental implants application. in this respect, zirconia tetragonal stabilized with %3 yttrium, is of great importance among the ceramic materials for endosseous dental implant application. because of its good mechanical properties and color similar to tooth. the aim and novelty of this study was to design and prepare y-t...

متن کامل

Effect of relative humidity on mechanical strength of zirconia/ Nafion® Nano-composite membrane

This paper presents the results of mechanical strength of wet and dry zirconia/ Nafion® nano-composite membrane. The tensile tests were conducted to determine elastic modulus and stiffness of dry and wet pristine Nafion® membrane and modified Nafion® membrane. The composite membranes were prepared by recast method of different synthesized zirconium oxide with the zirconia content of 10% by weig...

متن کامل

Influence of nano alumina coating on the flexural bond strength between zirconia and resin cement

PURPOSE The purpose of this in vitro study is to examine the effects of a nano-structured alumina coating on the adhesion between resin cements and zirconia ceramics using a four-point bending test. MATERIALS AND METHODS 100 pairs of zirconium bar specimens were prepared with dimensions of 25 mm × 2 mm × 5 mm and cementation surfaces of 5 mm × 2 mm. The samples were divided into 5 groups of 2...

متن کامل

Effect of Sandblasting Angle and Distance on Biaxial Flexural Strength of Zirconia-based Ceramics.

AIM Surface treatment is necessarily required for bonding of zirconia to the veneering porcelain and luting cements. Sandblasting is the most common and probably the most efficient surface treatment method. Sandblasting roughens the surface and may affect the flexural strength of zirconia. Different sandblasting protocols may yield variable results. This study sought to assess the effect of san...

متن کامل

Effect of Calcination Temperature on the Alumina-Zirconia Nanostructures Prepared by Combustion Synthesis

In this research, a sol gel autocaombustion route has been proposed to synthesize alumina-zirconia composite powders, using ammonium bicarbonate as a new fuel. Then the effect of calcination temperature on phase transformation and crystallite sizes was investigated. To characterize the products XRD, TEM and BET analyses were used. XRD patterns of as-synthesized powder and calcined powders at 11...

متن کامل

Synthesis and Characterization of Silver and Gold Nano-Structures on Chitosan-Porous Anodic Alumina Nano-Composite

This study was designed to probe the fabrication of unique silver and gold nano-structures engaging a self-designed chitosan-porous anodic alumina nano-composite as a template. Porous anodic alumina has been manufactured by di-step aluminum anodization in an oxalic acid electrolytic bath. The surface properties of porous anodic alumina were reinforced by chitosan neutralized in sodium hydro...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 49  شماره 2

صفحات  103- 111

تاریخ انتشار 2016-12-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023