Effect of Current Density and Surface Preparation of Steel on Morphology and Texture of Zinc Electrodeposits

نویسندگان

  • A. Saatchi and M. A. Golozar
  • K. Raeissi
چکیده مقاله:

On electropolished steel at low current densities, morphology and texture of electrodeposited zinc were investigated. Zinc coating is consisted of hexagonal crystallites laid on each other to produce packets. These packets are of different sizes and are stacked in different orientations to construct a homogeneous coating on steel substrate. This coating does not have texture, i.e., it has a random texture. With increasing current density, the morphology changes completely as each grain attains a special orientation. In this case, coating has a strong basal plane (0002) along with low angle planes (1013 and 1014). Coating obtained on mechanically polished surfaces consists of individual packets of zinc crystals, which are near each other with different &#10&#10orientations. These coatings have a higher density of basal plane (0002) in comparison to electropolished surfaces. The morphology and texture variations with cathodic polarization and surface preparation of steel are due to their effect on nucleation and growth.&#10

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

The Effect of Current Density on Morphology and Texture of Zinc Electrodeposit on Steel

Zinc was electrodeposited from an acidic sulphate solution on commercial steel sheet substrates galvanostatically at 10, 20, and 100 mA/cm2. The steel substrates had an average roughness number of 1.34 microns and a high percentage of its grains had their (111) planes parallel to the plate surface. During electrodeposition at 10 mA/cm2, on some specimens, there was an intense potential fluctuat...

متن کامل

The Effect of Current Density on Morphology and Texture of Zinc Electrodeposit on Steel

Zinc was electrodeposited from an acidic sulphate solution on commercial steel sheet substrates galvanostatically at 10, 20, and 100 mA/cm2. The steel substrates had an average roughness number of 1.34 microns and a high percentage of its grains had their (111) planes parallel to the plate surface. During electrodeposition at 10 mA/cm2, on some specimens, there was an intense potential fluctuat...

متن کامل

effect of seed priming and irrigation regimes on yield,yield components and quality of safflowers cultivars

این مطالعه در سال 1386-87 در آزمایشگاه و مزرعه پژوهشی دانشگاه صنعتی اصفهان به منظور تعیین مناسب ترین تیمار بذری و ارزیابی اثر پرایمینگ بر روی سه رقم گلرنگ تحت سه رژیم آبیاری انجام گرفت. برخی از مطالعات اثرات سودمند پرایمینگ بذر را بر روی گیاهان مختلف بررسی کرده اند اما در حال حاضر اطلاعات کمی در مورد خصوصیات مربوط به جوانه زنی، مراحل نموی، عملکرد و خصوصیات کمی و کیفی بذور تیمار شده ژنوتیپ های م...

EFFECT OF SUBSTRATE TEXTURE AND DEPOSITION CURRENT DENSITY ON PROPERTIES OF NiNANOCRYSTALLINE ELECTRODEPOSITS

Abstract: Nickel was electrodeposited onto copper substrates with high {111} and {400} peak intensities. The grain size of coatings deposited onto the copper substrate with a higher {111} peak intensity was finer. Spheroidized pyramid morphology was obtained at low current densities on both copper substrates. By increasing the deposition current density, grain size of the coating was increased ...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 23  شماره 2

صفحات  173- 184

تاریخ انتشار 2005-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

کلمات کلیدی

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023