Experimental study of fracture mechanics in the aluminum matrix composites containing Fifteen percent silicon carbide particles

نویسندگان

Mehdi Etaee M.Sc. Student, Rajai University

Mohammad Ranjbaran Assistant Porfessor, Rajai University

Mohammad Taghi Najafi M.Sc. Student, Rajai University

Rasul Amini Assistant Porfessor , Shiraz university

چکیده مقاله:

In this investigation ‚the fracture toughness of A356 containing15%SiC composite was studied. Al/SiC composites have been considered because of their mechanical and erosion properties .Low fracture toughness in Al/SiC as compared with Aluminium alloys is one of its disadvantage. In this study at first A356 alloy was melted in a smelting electrical furnace then poured into the mould. A356-15% SiC were composed by melting method and mixing continuously (in order not to precipitate SiC to the bottom) in the presence of a nature gas. The melt was poured in a metallic mould, then specimens were cut from the products bars in order to calculate fracture toughness according to ASTM. Obtained results for different specimens compared together. In this study Crack Opening Displacement (COD) is used to determine fracture toughness rate. KIc was calculated in composites and compared with that of base alloy. As a result KIc in composite samples were decreased significantly, debris, cracks, gas cavity.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Circumstellar aluminum oxide and silicon carbide in interplanetary dust particles

A systematic NanoSIMS isotope imaging study of sub-micrometer phases in interplanetary dust particles (IDPs) has led to the discovery of two presolar grain types that previously were observed only in primitive meteorites. A 350 · 600 nm Al2O3 grain has a large O enrichment and a slight O depletion, as well as a Mg excess due to the decay of extinct Al. Because of its relatively large size and p...

متن کامل

Combustion Synthesis of Titanium-Tungsten Carbide Composites in Iron Matrix

Combustion synthesis has been used to produce Fe-(Ti,W)C composites. A simple reactor was designed which made it possible to ignite the samples under controlled atmosphere. Samples with different W/Ti ratio were ingnited under argon atmosphere by an electric arc and a self-propagating reaction was initiated in each sample. Different composites such as WC in Fe-Ti matrix, WC+(Ti,W)C in Fe matrix...

متن کامل

Combustion Synthesis of Titanium-Tungsten Carbide Composites in Iron Matrix

متن کامل

Finite Fracture Mechanics of Matrix Microcracking in Composites

The first form of damage in composite laminates is often matrix microcracks that are defined as intralaminar or ply cracks across the thickness of the ply and parallel to the fibers in that ply (see reviews in [1,2]). Tensile loading, fatigue loading, environment, and thermal cycling can all lead to microcrack formation. Microcracks can form in any ply that has a significant component of the ap...

متن کامل