Investigating Tribological Characteristics of Ni-P and Double–Layered Ni-P/Ni-B Electroless Coatings Applied to the Carbon Mild Steel Ck45

نویسندگان

  • A. Baibordi Department of Materials Engineering, Shiraz University, Shiraz, Iran
  • A. Dehghan Department of Materials Engineering, Shiraz University, Shiraz, Iran
  • K. Amini Department of Engineering, Tiran Branch, Islamic Azad University, Tiran, Iran
  • M. Bina Department of Advanced Materials and Renewable Energy, Iranian Research Organization for Science and Technology, Tehran, Iran
چکیده مقاله:

In this research, tribological characteristics of Ni-P electroless coating and double-layered Ni-P/Ni-B electroless coating were studied. For this purpose, Ni-P electroless coating with 25 μm thickness was initially applied to the surface of steel Ck45 samples; then, a double-layered Ni-P/Ni-B electroless coating, including inner layer of Ni-P with 15 μm thickness and outer layer of Ni-B with 10 μm thickness, was applied to the surface of similar samples and were heat treated at 400˚C for 1 h. Effect of heat treatment on morphology, structural variations and wear behavior of coating was investigated using different tests such SEM, XRD and pin on disk wear test at room temperature. Hardness of the obtained coatings was measured by a Vickers microhardness machine prior and after heat treatment of the samples. The results showed that the double-layer coating with the same thickness in each layer improved hardness and wear resistance compared to the single-layer coating. Heat treatment led also to the creation of nano crystalline structure; therefore, hardness and wear resistance of the coating increased due to change in structure from amorphous to crystalline structure and created rigid phases of Ni3P.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

investigating tribological characteristics of ni-p and double–layered ni-p/ni-b electroless coatings applied to the carbon mild steel ck45

in this research, tribological characteristics of ni-p electroless coating and double-layered ni-p/ni-b electroless coating were studied. for this purpose, ni-p electroless coating with 25 μm thickness was initially applied to the surface of steel ck45 samples; then, a double-layered ni-p/ni-b electroless coating, including inner layer of ni-p with 15 μm thickness and outer layer of ni-b with 1...

متن کامل

Electroless Ni–P composite coatings

This review outlines the development of electroless Ni–P composite coatings. It highlights the method of formation, mechanism of particle incorporation, factors influencing particle incorporation, effect of particle incorporation on the structure, hardness, friction, wear and abrasion resistance, corrosion resistance, high temperature oxidation resistance of electroless Ni–P composite coatings ...

متن کامل

CORROSION BEHAVIOR OF ELECTROLESS Ni-P/NANOZnO COATINGS

Abstract:Electroless Nickel-phosphorus (EN) coatings provide high performance in various industrial fields due to their unique properties such as excellent corrosion and wear resistance. This paper aims to study the effect of ZnO nano-particles addition on corrosion behavior of EN coatings. Various amounts of ZnO nano-particles with average diameter of 50 nm were added to hypophosphite reduced ...

متن کامل

INVESTIGATION OF THE MECHANICAL, CORROSION PROPERTIES AND WEAR BEHAVIOUR OF ELECTROLESS Ni-P PLATED MILD STEEL

In the present study the mild steel (MS) specimens were coated with Nickel-Phosphorus (Ni-P) using acrylic bath. Heat treatment was carried out on specimens under different temperatures and time periods in an inert atmosphere. The various mechanical and tribological tests were performed on specimens. Using weight loss method, the corrosion nature of the samples under different environments was ...

متن کامل

Roughness Optimization of Electroless Ni-B Coatings Using Taguchi Method

In this paper, the authors present an experimental study of roughness characteristics of electroless Ni-B coatings and optimization of the coating process parameters based on L27 Taguchi orthogonal design. Three coating process parameters are considered viz. bath temperature, reducing agent concentration, and nickel source concentration. It is observed that concentration of reducing agent toget...

متن کامل

Shot Peening as an Alternative to Fatigue Life Improvement of CK45 Steel Coated with an Electroless Ni-Cu-P

The effect of an electroless Ni-Cu-P coating on the fatigue behavior of quenched and tempered CK45 steel has been investigated. The fatigue tests under rotating bending conditions have been conducted in three different conditions of uncoated, as-deposited and shot peened prior to the coating deposition. The results indicate that plating of the base steel leads to a fatigue life reduction. The d...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 9  شماره 2

صفحات  1- 4

تاریخ انتشار 2012-12-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023