Preparation and Mechanical Properties of Nano/Ultrafine Bainitic Structure in AISI 52100 Steel

نویسندگان

  • M. Nourbakhsh Department of Material Engineering, Malek- Ashtar University of Technology (MUT), Shahin-Shahr, Isfahan, Iran
  • M. Tavoosi Department of Material Engineering, Malek- Ashtar University of Technology (MUT), Shahin-Shahr, Isfahan, Iran
  • S.R. Hosseini Department of Material Engineering, Malek- Ashtar University of Technology (MUT), Shahin-Shahr, Isfahan, Iran
چکیده مقاله:

The development of nano/ultrafine bainitic structure in AISI 52100 steel was the goal of this study. For this purpose,the AISI 52100 the specimens were austenitized at 1050 °C for 60 min followed by low-temperature austemperingtreatment at different temperatures and times. The austempered samples were characterized using field emissionscanning electron microscopy (FESEM), X-ray diffraction (XRD) and tension test. According to achieved results,the microstructure of AISI 52100 steel after the austempering treatment consisted of ultrafine bainitic ferrite platesand retained austenite with two morphologies of micrometer-block and fine film. At the austempering temperatureup to 250 °C, the micrometer-blocky morphology of austenite completely vanished from the microstructure, andthe strength and ductility increased to about 2000 MPa and 7 %, respectively. By increasing the austemperingtemperature to 300 °C, the strength and ductility reduced (to about 1808 MPa and 3 %) simultaneously as a resultof changing in the shape and size of bainite phase.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

preparation and mechanical properties of nano/ultrafine bainitic structure in aisi 52100 steel

the development of nano/ultrafine bainitic structure in aisi 52100 steel was the goal of this study. for this purpose,the aisi 52100 the specimens were austenitized at 1050 °c for 60 min followed by low-temperature austemperingtreatment at different temperatures and times. the austempered samples were characterized using field emissionscanning electron microscopy (fesem), x-ray diffraction (xrd...

متن کامل

Development of Ultrafine Bainitic Structure in AISI 431 Stainless Steel

The development of ultrafine bainitic structure in AISI 431 stainless steel was the goal of this study. For this purpose, the AISI 431 specimens were austenitized at 1100 °C for 60 min followed by low-temperature austempering treatment at different temperatures and times. Austempered samples were characterized using field emission scanning electron microscopy (FESEM), X-ray diffraction (X...

متن کامل

Nanostructured bainitic steel obtained by powder metallurgy approach: structure, transformation kinetics and mechanical properties

A PM approach is investigated in the context of extremely fine low temperature bainitic steels with a reasonable combination of ultimate tensile strength and uniform elongation. The strategy consists of three steps. First, ball milling is used for mechanical alloying and to create a large density of interfaces prior to sintering. In the second step, spark plasma sintering is used as a rapid con...

متن کامل

determination of some physical and mechanical properties red bean

چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...

15 صفحه اول

Mechanical Properties of Boronized AISI 316, AISI 1040, AISI 1045 and AISI 4140 Steels

In this study, some mechanical properties of borided and unborided four steels were investigated. Boronizing of steels was performed by powder pack method at 1210 K for 4 h. The hardness of borides, boride layer thickness and room temperature tensile properties were measured and it was observed that hardness and tensile properties strongly depend on chemical composition of steels. In addition, ...

متن کامل

Improving the Microstructure, Mechanical and Magnetic Properties of AISI 4340 Steel Using the Heat Treatment Process

AISI 4340 steel is one of the super strong steels that can be selected for different applications. By designing the proper cycles of heat treatment, the optimum microstructure and properties of this steel can be achieved. In this study, different heat treatment cycles were introduced to achieve the optimum microstructure and improve the mechanical and magnetic properties of AISI 4340 steel. The...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 13  شماره 2

صفحات  31- 39

تاریخ انتشار 2016-12-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023