Synthesis of Nano-Sized Titania Particles by Hydrolysis of Titanium Tetrachloride

نویسندگان

  • M. Farahmandjou Department of Physics, Varamin-Pishva Branch, Islamis Azad University, Varamin, Iran
  • M. Ramazani Department of Physics, Varamin Pishva Branch, Islamis Azad University, Varamin, Iran
چکیده مقاله:

Nano-sized titanium dioxide TiO2 powder was successfully prepared from its precursor titanium (IV) chloride by a simple and new wet chemical method. TiCl4 were used as precursor in hydrogen peroxide, H2O2 and ethanol. This solution was then peptized using nitric acid and heated under reflux at 80°C. Their physico-chemical properties were then characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM) and X-Ray diffraction (XRD). The TEM results showed that the size of as-synthesized TiO2 nanoparticles were in the range of 7-10 nm. The SEM images showed that the size of nanoparticles increased when the nanoparticles prepared in presence of nitric acid. The SEM images showed that the quality of annealed TiO2 nanoaprticles, increased when the nanoparticles synthesized without nitric acid. The crystal structure of the nanoparticles before and after annealing was done by XRD analysis. It was realized that the rutile phase was formed after heat treatment at 600°C. XRD pattern also showed that the size of annealed TiO2 nanoparticles increased from 20 to 50 nm when the nanoparticles prepared with nitric acid.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

synthesis of nano-sized titania particles by hydrolysis of titanium tetrachloride

nano-sized titanium dioxide tio2 powder was successfully prepared from its precursor titanium (iv) chloride by a simple and new wet chemical method. ticl4 were used as precursor in hydrogen peroxide, h2o2 and ethanol. this solution was then peptized using nitric acid and heated under reflux at 80°c. their physico-chemical properties were then characterized by transmission electron microscopy (t...

متن کامل

synthesis of amido alkylnaphthols using nano-magnetic particles and surfactants

we used dbsa and nano-magnetic for the synthesis of amido alkylnaphtols.

15 صفحه اول

extraction and characterization of allium irancum plant extract and its application in the green synthesis of silver nano particles and oxidation of thiocarbony1 compounds

سنتز سبز نانوذرات فلزی (nps) درسالهای اخیر توجه بسیارزیادی را به خود جلب کرده است. زیرا این پروتوکل کم هزینه وسازگار با محیط زیست از روش های استاندارد سنتز. در این پایان نامه ما گزارش میکنیم یک روش ساده و سازگار با محیط زیست برای سنتز نانوذرات نقره با استفاده از محلول آبی عصاره گیاه allium iranicum به عنوان یک عامل کاهش دهنده ی طبیعی. نانو ذرات نقره مشخص شد با استفاده از تکنیک های uv-visible، x...

Synthesis of Chromium Oxide Nano Particles by Thermal Decomposition Method

Disclosed is a method of preparing pigmentary chromium oxide nano particles having 50 percent particle size less than about 100 nm. Preparation of nano chromium (III) oxide is investigated by thermal decomposition method. According to the disclosed method, a substantially dry solid composition of potassium dichromate and carbon active is heated in CO2 atmosphere to a temperature of about 60...

متن کامل

Preparation and Characterization of Titania Nanoparticles from Titanium Tetrachloride and Titanium Sulfate Flocculation of Dye Wastewater

Pollutants in dye wastewater significantly vary due to the large number of dyes and other chemical compounds used in dyeing processes. The major compounds in dye wastewater are desizing and scouring agents, bleaches, reducing agents, detergents and wetting agents, finishing agents, organic acids and dyes, and fluorescent brighteners1). Physical, chemical and biological methods have been applied...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 4  شماره 1

صفحات  31- 34

تاریخ انتشار 2015-04-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023