Tribological Behaviour of Fe-Al Intermetallic Compound Coated Carbon Tool Steel

نویسندگان

  • M. Salehi and F. Ashrafizadeh
  • M. Shamanian
چکیده مقاله:

The use of Fe-Al intermetallic compound coatings has been investigated in order to improve the tribological behaviour of carbon tool steel. The coatings were formed by a pack cementation process and subsequently diffusion annealing at 900˚C in an argon controlled atmosphere. The optimum diffusion time was selected on the basis of optimum thickness and tribological behaviour. The microstructure and the phases developed on the surface were identified by metallography, microhardness, X-ray diffraction (XRD), microanalysis (EDX) and glow discharge optical spectroscopy (GDOS) techniques. Experimental results indicate that a three layer coating is formed on the surface of the aluminized specimens, the outermost layer being identified as Fe2Al5 and the underlying layers as FeAl and Fe3Al. A two layer coating was formed on the surface of the aluminized and subsequently diffusion annealed specimen at the optimum time. The FeAl and Fe3Al have been formed on and below the surface, respectively. The results from wear testing indicate that these coatings improve the wear and frictional behaviour of carbon steel significantly. The predominant wear mechanisms of diffusion annealed specimens were identified as delamination and oxidative wear.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

tribological behaviour of fe-al intermetallic compound coated carbon tool steel

the use of fe-al intermetallic compound coatings has been investigated in order to improve the tribological behaviour of carbon tool steel. the coatings were formed by a pack cementation process and subsequently diffusion annealing at 900˚c in an argon controlled atmosphere. the optimum diffusion time was selected on the basis of optimum thickness and tribological behaviour. the microstructure ...

متن کامل

Magnetic behaviour of the intermetallic compound YbCo2Si2

We report on a comprehensive study of the magnetic properties of YbCo2Si2 investigated using a single crystal. All data confirm a stable trivalent Yb state carrying a well-localized 4f moment, as well as a non-magnetic Co state. We observed a sizeable anisotropy in the magnetic susceptibility χ(T ), with the moment in the basal plane twice as large as that along the c-direction. Combining this ...

متن کامل

Surface Characterization and Tribological Behaviour of Ti-Ni-P Intermetallic Coatings on Titanium Alloys

In this research, tribological behavior of Ti-Ni-P intermetallic coatings on titanium substrates have been investigated under dry reciprocating conditions. Hardness profile testing results exhibit that high surface hardness has been attained and static indentation result shows that the intermetallic coating has better adhesion strength than the conventional ceramic coatings. In this respect, th...

متن کامل

Surface Characterization and Tribological Behaviour of Ti-Ni-P Intermetallic Coatings on Titanium Alloys

In this research, tribological behavior of Ti-Ni-P intermetallic coatings on titanium substrates have been investigated under dry reciprocating conditions. Hardness profile testing results exhibit that high surface hardness has been attained and static indentation result shows that the intermetallic coating has better adhesion strength than the conventional ceramic coatings. In this respect, th...

متن کامل

Control of Formation of Intermetallic Compound in Dissimilar Joints Aluminum-steel

The elimination of the FexAly type phases was considered the solution to low ductility presented in aluminum-steel welded joints. Recently, the researches do not seek the suppression but the control of the thickness of these compounds. In this work, Al-Fe joints were manufactured by solid state and fusion welding, looking for controlling the formation of intermetallic comp...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 16  شماره 2

صفحات  81- 93

تاریخ انتشار 1998-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

کلمات کلیدی

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023