Annealing temperature effect on nanostructure and phase transition of Copper Oxide thin films

نویسندگان

  • A. Behju Department of Chemistry, Chalous branch, Islamic Azad University, Chalous, Iran.
  • K. Khojier Department of Physics, Chalous branch, Islamic Azad University, Chalous, Iran.
چکیده مقاله:

This paper addresses the annealing temperature effect on nanostructure and phase transition of copper oxide thin films, deposited by PVD method on glass substrate (at 110 nm thickness) and post annealed at different temperatures (200-400°C) with a flow of 1 cm3s-1 Oxygen. The X-ray diffraction (XRD) was employed for crystallographic and phase analyses, while atomic force microscopy (AFM) was used for morphology investigation. The results showed (CuO2) cuprite phase for samples annealed at 200 and 250°C and (CuO) tenorite phase for samples annealed at 350 and 400°C, while sample annealed at 300°C had a complex phases (CuO2 and CuO). The size of the grains increased, but roughness increased and then decreased by increasing of annealing temperature. Furthermore, calculated activation energy from grain diameter (at arrhenius plot) was 0.54 eV.  

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

annealing temperature effect on nanostructure and phase transition of copper oxide thin films

this paper addresses the annealing temperature effect on nanostructure and phase transition of copper oxide thin films, deposited by pvd method on glass substrate (at 110 nm thickness) and post annealed at different temperatures (200-400°c) with a flow of 1 cm3s-1 oxygen. the x-ray diffraction (xrd) was employed for crystallographic and phase analyses, while atomic force microscopy (afm) was us...

متن کامل

Formation of Cupric Oxide Films on Quartz Substrates by Annealing the Copper Films

In the present work, cupric oxide (CuO) films were obtained through thermal annealing of the copper (Cu) films deposited on quartz substrates by DC magnetron sputtering method. The annealing was performed in air atmosphere for different times ranging from 60-240 min at temperature of 400 ºC. The influence of annealing times on structural and morphological properties of the films was investi...

متن کامل

Structural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films

Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...

متن کامل

Structural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films

Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...

متن کامل

Effect of Annealing Temperature on the Structural, Magnetic and Optical Properties of SrCo2Fe16O27 Hexaferrite Nanostructure

In this paper, W-type SrCo2Fe16O27 hexaferrite nanostructures were synthesized by sol-gel auto-combustion method. Effect of annealing temperature on the structural, magnetic and optical properties of these SrCo2Fe16O27 nanostructures was investigated. In order to determine the annealing temperature of samples, the prepared gel was examined by thermo-gravimetric and differential-thermal analyses...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ذخیره در منابع من قبلا به منابع من ذحیره شده

{@ msg_add @}


عنوان ژورنال

دوره 2  شماره 3

صفحات  185- 190

تاریخ انتشار 2012-03-01

با دنبال کردن یک ژورنال هنگامی که شماره جدید این ژورنال منتشر می شود به شما از طریق ایمیل اطلاع داده می شود.

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023