Mehdi Pourabdoli
Department of Metallurgy and Materials Engineering, Hamadan University of Technology, Hamadan, Iran
[ 1 ] - Effects of Fe2O3 addition and mechanical activation on thermochemical heat storage properties of the Co3O4/CoO system
Effects of Fe2O3 addition (2-20 wt%) with 1 h mechanical activation on redox reactions of Co3O4 were studied by TG/DSC, SEM, and XRD analyses. The results showed that a Fe2O3 addition from 2 to 15 wt% increases the oxygen release from 1.4 to 3.4 wt% and decreases the reduction onset temperature from 1030 to 960 °C, while it increases the oxygen uptake value and re-oxidation onset temperature re...
[ 2 ] - Isothermal Redox Kinetics of Co3O4-Fe2O3 Nano-Composite as a Thermochemical Heat Storage Material
Isothermal redox kinetics of as-received Co3O4 (AC), 1 h ball milled Co3O4 (BC), and 1 h ball milled Co3O4-15wt.% Fe2O3 (BCF) was investigated at various temperatures (1130, 1100, 1070, and 1040 °C for reduction and 830, 860, and 890°C for re-oxidation) by thermogravimetric method. It was found that mechanic...
[ 3 ] - Effect of Mechanical Activation on the Kinetics of Ammoniacal Thiosulfate Leaching of a Refractory Oxide Gold Ore
The effect of mechanical activation on the kinetics of ammoniacal thiosulfate leaching of a refractory oxide gold ore containing 2.8 ppm Au was investigated. The gold extraction of 99.81% was achieved by 16 h leaching of a sample mechanically activated for 60 minutes. The gold extraction observed for a similar reference sample without mechanical activation was only 55%. Studies revealed that le...
[ 4 ] - Thermochemical Heat Storage Properties of Co3O4-X wt % Al2O3 and Co3O4-X wt % Y2O3 Composites (X=1, 2, 5, 8, 10)
The effect of Al2O3 (1-10 wt %) and Y2O3 (1-10 wt %) additions on thermochemical heat storage properties of Co3O4/CoO system was investigated by thermogravimetry, XRD, and SEM analyses. Results showed that the addition of Al2O3 to Co3O4 at constant 8 h mechanical activation improved the...
[ 5 ] - مقایسه روش های تهیه پودر کامپوزیتی Co3O4- Fe2O3 به عنوان ماده ذخیره کننده انرژی حرارتی و مطالعه مورفولوژی و تغییر فاز آن در طی واکنش های احیا – اکسیداسیون
در این تحقیق پودر کامپوزیتی Co3O4 حاوی 15 درصد وزنی Fe2O3 به دو روش کلی شامل الف- آسیاکاری هم زمان (0، 1 و 16 ساعت) مخلوط اکسید ها و ب- آسیاکاری جداگانه اکسید کبالت (0، 1 و 16 ساعت) و اکسید آهن (0، 5/0 و 7 ساعت) و سپس مخلوط کردن آنها، تهیه و از نظر اندازه متوسط ذرات، مورفولوژی ذرات، نحوه پخش ذرات فاز ثانویه (اکسید آهن)، آنالیز فازی و ظرفیت ذخیره انرژی حرارتی به روش های FE-SEM، XRD و ترموگراویمت...
[ 6 ] - بررسی اثر TiO2 بر خواص دفع هیدروژن از Al3Mg2
مطالعات نشان داده‌اند که ترکیبات پایه منیزیم می‌توانند در ذخیره سازی هیدروژن در حالت جامد استفاده شوند. در این پژوهش ترکیب بین فلزی Al3Mg2 به روش ریخته‌گری تهیه گردید. سپس نمونه‌هایی از این ترکیب تحت اتمسفر هیدروژن و در زمان‌های مختلف آسیاکاری شدند. نتایج حاصل از آزمایش گرماسنجی جرمی و پراش اشعه ایکس نشان داد که بیشترین میزان ذخیره سازی هیدروژن پس از 2 ساعت آسیاکاری در محیط این گاز بوده و کاه...