[ 1 ] - بررسی ویژگی‌های مغناطیسی کامپوزیت‌های نرم مغناطیسی پایه آهن پوشش داده‌ شده با عایق سیلیکات سدیم

In this study, iron powder (~45 μm) with the  minimum purity of 99% was insulated by the 1 to 4 wt% sodium silicate insulator (SiO2.3Na2O solution in 40 wt% water) and the 0.5 wt% zinc stearate. Insulated powders were pressed in a die with  a toroidal shape at the pressure of 320 MPa. The effects of insulator percentage and annealing temperature on the magnetic permeability, core l...

[ 2 ] - A Comparative Study of Insulators on Magnetic Properties of Sendust Based Nanocomposite Powder Cores

In this study, Sendust (Fe85Si9.6Al5.4) nanostructure alloy was prepared bymechanical alloying and was characterized by X-ray diffraction. In addition, the alloy’smorphology and its distribution particle size were investigated by scanning electronmicroscopy method. The alloyed powders were insulated with 4wt% of three differentinsulating materials including polyvinyl alc...

[ 3 ] - In-situ reactive synthesis of full dense Si2N2O by incorporating of Amourphous nanosized Si3N4;effect of MgO and Y2O3

Si2N2O is considered as a new great potential structural/functional candidate in place of Si3N4. The amorphous Si3N4 nanopowder was incorporated into silica sol by adding of MgO and Y2O3 as sintering aid. Synthesized powders were heated by spark plasma sintering at a heating rate of 100 oC/min yielded fully dense compacts at 1550 and 1750 oC for 40 min. The phase formation of samples was charac...

[ 4 ] - Fabrication and Investigation of Se-Ge Glass-Ceramics in the Presence of Ga and Sn Additives

The Chalcogenide glasses were fabricated by melting and quenching techniques in the Se-Ge system at the presence of 1mol% Ga and 3, 5, and 7mol% Sn. Differential Scanning Calorimetry (DSC) analysis was conducted to extract the heat treatment of the samples. Fourier Transform Infrared (FTIR) spectroscopy analysis was also performed in a range of 2-16µm. The Glass samples were heat-treated at 450...

[ 5 ] - Comparison of Semiconducting Behavior and Optical Properties of Oxyfluoride Glasses of SiO2-Al2O3-BaF2 and SiO2-Al2O3-CaF2 Systems

Amorphous semiconductors are materials with a brilliant prospect for a wide range of optical applications like solar cells, optical sensors, optical devices, and memories. The purpose of the present research was to study the semiconducting optical properties of SiO2-Al2O3-CaF2 and SiO2-Al2O3-BaF2 oxyfluoride...

[ 6 ] - An Investigation into the Effects of Composition and BaF2 Content on the Structure and Crystallization Behavior of SiO2-Al2O3-K2O-BaF2 Oxyfluoride Glasses

Nowadays, oxyfluoride glasses have received much attention from photonic researchers as they benefit from the advantages of both oxide and fluoride glasses (low phonon energy in parallel with high mechanical and chemical durability). The purppose of this paper was to study the different glass compositions in SiO2-Al2O3-K2O-BaF2 system and i...