[ 1 ] - Fabrication of Nb/V co-doped TiO2 thin films and study of structural, optical and photocatalytic properties
In this study, different samples of Niobium and Vanadium co-doped titania thin films (5-10-15 mol% Nb and 5-10-15 mol% V) were prepared via sol−gel dip coating method, using niobium chloride as niobium precursor, ammonium metavanadate as vanadium precursor, and titanium (IV) butoxide (TBT) as titanium precursor. The effects of doping amount on the structural, optical, and photo-catalytic prope...
[ 2 ] - Fabrication of Nb/V co-doped TiO2 thin films and study of structural, optical and photocatalytic properties
In this study, different samples of Niobium and Vanadium co-doped titania thin films (5-10-15 mol% Nb and 5-10-15 mol% V) were prepared via sol−gel dip coating method, using niobium chloride as niobium precursor, ammonium metavanadate as vanadium precursor, and titanium (IV) butoxide (TBT) as titanium precursor. The effects of doping amount on the structural, optical, and photo-catalytic prope...
[ 3 ] - بررسی دمای کلسینهشدن بر ویژگی ساختاری، نوری و فتوکاتالیستی نانوذرات مزومتخلخل تیتانیا
در این پژوهش، نانوذرات مزومتخلخل تیتانیم دی‌اکسید به روش سل‌ژل تهیه شد. اثر دمای کلسینهشدن بر ویژگی ساختاری، فتوکاتالیستی و نوری نانوذرات مورد بررسی قرارگرفت. از تترابوتیل اورتوتیتانات (TBT) به‌عنوان پیش ماده تیتانیم و از اتانول به‌عنوان حلال استفاده شد. از آزمون گرماوزنسنجی-تجزیه گرمایی تفاضلی (TG-DTA) برای انتخاب گستره مناسب دمایی کلسینهشدن، پراش پرتو ایکس (XRD) برای تعیین فازها، روش جذب ...