The present work is aimed at examining carbon steel oil pipelines corrosion using three natural extracts (Eruca Sativa, Rosell and Mango peels) that are used as inhibitors of different concentrations ranging from 0.05-0.1wt. %. Two sulphur compounds are used as corrosion mediums. Weight loss method was used for measuring the corrosion rate of the carbon steel specimens immersed in technical whi...

We report a unique and highly stable electrocatalyst-platinum (Pt) supported on titanium-ruthenium oxide (TRO)-for hydrogen fuel cell vehicles. The Pt/TRO electrocatalyst was exposed to stringent accelerated test protocols designed to induce degradation and failure mechanisms identical to those seen during extended normal operation of a fuel cell automobile-namely, support corrosion during vehi...

The relationship between dissolved oxygen (DO) and corrosion behavior of X80 steel in acidic soil simulated solution was studied by potentiodynamic polarization curves, electrochemical impedance spectroscopy (EIS), scanning Kelvin probe technique (SKP) and X-ray diffraction (XRD). Results showed that the presence of DO accelerated the cathodic process of corrosion for X80 steel in the acidic so...

in this study, the effects of forming method (extrusion) and environmental factors (solution ph and temperature) on the corrosion performance of az91 magnesium alloys were investigated using potentiodynamic polarization, electrochemical impedance spectroscopy (eis), scanning electron microscopy (sem) and salt spray techniques. the polarization test results of the specimens showed that simple sh...

This study provides a semi-probabilistic approach to durability design of reinforced concrete structures, subjected carbonation-induced corrosion. The method was developed from an existing and using comprehensive data collated the literature. A statistical model for predicting accelerated carbonation coefficient, as input variables mix proportions test conditions also generated. performance pro...

Recent advancements in metal fibers have introduced a promising new type of stainless steel fiber with high stiffness, high failure strain, and a thickness < 100 μm (<0.00394 in.) that can be utilized in a steel fiber-reinforced polymer. However, stainless steel is known to be susceptible to pitting corrosion. The main goal of this study is to compare the impact of corrosion on the mechanical p...

The Brillouin optical time-domain analysis (BOTDA)-based optical fiber method has been proposed to measure strain variations caused by corrosion expansion. Spatial resolutions of 1 m can be achieved with this kind of Brillouin sensor for detecting the distributed strain. However, when the sensing fiber is wound around the steel rebar in a number of circles in a range of several meters, this spa...

Ferrocement as a form of reinforced concrete constructed of hydraulic cement mortar strengthened with closely spaced layers of continuous and relatively small diameter wire mesh. It has been used worldwide as a construction material to provide better construction and rehabilitation of structures. Moreover, there may be structural deterioration of ferrocement due to the exposure of saline water....

This study presents the effect of corrosion prestressed concrete (PC) strands on prestressing force and reduction mechanism uniaxial force. A total 14 was tested by combining a rigid frame testing machine with an electrified accelerated device. The specimens were divided into two groups having levels 70% 50% tensile strength PC strands. expected degree specimens, which defined mass loss, calcul...