The fatigue micro crack initiation and propagation tests of a TiAl alloy with 8% Nb content were carried out by using scanning electron microscopy in situ technology at room temperature and at 750 C. These results indicated that the fatigue micro crack initiation was mainly caused by the stress concentration at room temperature, but at an elevated temperature (750 C) the multi-cracks were cau...

In this paper we propose a spatial model for the initiation of cracks in the bone cement of hip replacement specimens. The failure of hip replacements can be attributed mainly to damage accumulation, consisting of crack initiation and growth, occurring in the cement mantle that interlocks the hip prosthesis and the femur bone. Since crack initiation is an important factor in determining the lif...

The work involves develops attended by a numerical execution of the eXtend Finite Element Method premises a measurement by the fracture process cracked so many cracked plates an application will be processed for the calculation of the stress intensity factor SIF. In the first we give in statically part the distribution of stress, displacement field and strain of composite plate in two cases unc...

The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy 2024 was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact su...

In situ ultrasonic fatigue with a cyclic frequency of 20 kHz was employed in an environmental scanning electron microscope (ESEM) to characterize fatigue crack formation and growth in the near alpha titanium alloy Ti–6242S. The role of environment on small fatigue crack initiation and growth was investigated in vacuum and in variable pressures of saturated water vapor, as well as in laboratory ...

This paper presents a three-dimensional crack initiation analysis in a sidegrooved CT specimen. This is achieved with an endochronic damage model proposed recently by Chow and Chen [ 1,2] and discretized for finite element analysis. The damage model enables the quantification of the progressive damage evolution which would not be otherwise possible using the conventional fracture mechanics anal...

On the ground of manufacturing, sheet metal parts play a key role as they cover about half of the production processes. Sheet metals are commonly obtained from rolling and forming processes which causes misalignment of micro structure resulting obvious anisotropic characteristics and micro cracks. Presence of micro cracks poses serious attention, when stresses at the tip reach to the critical v...

Fatigue tests have been conducted on an advanced disc Ni-based superalloy (Low Solvus, High Refractory (LSHR) alloy) at 650 C in air under three-point bend loading to investigate the role of orientation-dependent grain boundary oxidation in crack initiation and early propagation. It is found that crack initiation occurs mainly from bulged grain boundary oxides, and cracks then predominantly pro...

The purpose of this study is to investigate bending moment and the axial load capacity of a pressurized pipe suffering from a through-wall circumferential crack repaired by a composite sleeve. The three-dimensional finite element method (FEM) was adopted to compute the results, and the failure assessment diagram (FAD) was employed to investigate the failure behavior of the repaired pipe. The fi...

In this paper the influence of microstructure on crack initiation stress and ultimate strength is investigated using results and analysis of 32 triaxial compression tests performed on cylindrical cores of dolomite samples which exhibit a wide range of grain sizes and mosaic textures. All tests were performed at a constant strain rate, under confining pressures between 0 to 40 MPa. The predictiv...