In the present work, we investigate the effect of "fatigue" on the fatigue behavior and atomic structure of Zr-based BMGs. Fatigue experiments on the failed-by-fatigue samples indicate that the remnants generally have similar or longer fatigue life than the as-cast samples. Meanwhile, the pair-distribution-function (PDF) analysis of the as-cast and post-fatigue samples showed very small changes...

Analysis has been performed on fracture initiation near a crack in a brittle material with strength described by Weibull statistics. This nonlocal fracture model allows for a direct correlation between near crack-tip stresses and failure. Predictions are made for both the toughness and average fracture initiation angle of a crack under mixed-mode loading. This is pertinent for composites and is...

Continuum approaches to fracture regard crack initiation and growth as the ultimate consequences of a gradual, local loss of material integrity. The material models which are traditionally used to describe the degradation process, however, may predict premature crack initiation and instantaneous, perfectly brittle crack growth. This nonphysical response is caused by localisation instabilities d...

Abstract Crack initiation and propagation in a peroxide-cured polybutadiene rubber reinforced with silanised silica nanofiller were studied under cyclic loading condition. The fatigue properties of the semi-transparent samples tested at constant strain amplitude, test frequency temperature. Initiation subsequent growth cracks observed using an optical microscope as function number cycles until ...

The typical experimental procedure for testing stress corrosion cracking initiation involves an interval-censored reliability test. Based on these test results, the parameters of a Weibull distribution, which is a widely accepted crack initiation model, can be estimated using maximum likelihood estimation or median rank regression. However, it is difficult to determine the appropriate number of...

A reliable and cost effective two-phase methodology is proposed to predict crack propagation in generic two-dimensional structural components under complex fatigue loading. First, the fatigue crack path and its stress intensity factors are calculated in a specialized finite element software, using small crack increments. At each crack propagation step, the mesh is automatically redefined based ...

Recent studies have shown that nanotwinned copper (NT Cu) exhibits a combination of high strength and moderate ductility. However, most engineering and structural applications would also require materials to have superior fracture toughness and prolonged subcritical fatigue crack growth life. The current study investigates the effect of twin density on the crack initiation toughness and stable ...

As fretting fatigue cracks are initiated at an early stage of life, the fretting fracture process is dominated by the stable growth of cracks. Hence the measurement of crack length is very important. This paper demonstrates the suitability of the DC potential drop technique for the measurement of fretting cracks. A calibration has been established for monitoring crack growth in BS L65 copper al...

Initial cracks occur in high strength concrete sleepers for various reasons, such as shrinkage and wrong curing and long lifetime of over 50 years of sleepers. These cracks may lead to complete failure of the structure. In order to more accurately design the sleepers, fracture mechanics (not strength of materials) should be incorporated. In order to achieve this purpose, it is important to fore...

Analysis of toughness in 6156 Al-Mg-Si-Cu sheet has been performed using enhanced Kahn tear tests on samples quenched at different rates. Crack initiation energies were hardly affected by changing water quench temperature from 20°C to 60°C; however a significant reduction was evident on air cooling. Crack propagation energy was reduced for both 60°C water quenched and air cooled materials. Obse...