Precracked and notched specimens were used to investigate the fracture mechanism of a bainite steel at low temperature. The critical fracture event was studied using metallographic sectioning method. The results showed that the critical cleavage event was different in the precracked and the notched specimens. At -196C, all specimens fractured at lower-shelf region without any ductile crack grow...

Fatigue crack growth was investigated in a 001 1⁄2 oriented single crystal specimen, made of a Ni-based superalloy, Haynes 230. Crack propagation was characterized with digital image correlation: crack closure, measured by analyzing the relative displacements of crack flanks, showed closure levels much lower than polycrystal alloys. Reversed plastic zones were calculated from regressed stress i...

In this study, the damage fields near the crack tip in edge-cracked sheet specimens subjected to a constant strain rate of 0.05 min were investigated using real-time radiographic techniques. During the tests, Lockheed-Martin Advanced Technology Center’s high-energy real-time x-ray system (HERTIS) was used to monitor damage initiation and evolution processes near the crack tip. The experimental ...

This paper investigates the phenomenon of slant fracture observed in stable tearing tests of many ductile materials, where an initially flat crack, loaded under remote Mode I conditions, tends to grow into a slant crack and stay in the slant configuration until final fracture. In an effort to identify potential reasons why cracks prefer to grow in a slant manner, three-dimensional finite elemen...

Fracture and breakage of single crystals, particularly of silicon wafers, are multi-scale problems: the crack tip starts propagating on an atomic scale with the breaking of chemical bonds, forms crack fronts through the crystal on the micrometre scale and ends macroscopically in catastrophic wafer shattering. Total wafer breakage is a severe problem for the semiconductor industry, not only duri...

Multi-layered systems used in automotive plain bearings show complex patterns of crack growth under service conditions. The studied architecture consists of a steel backing (1.8 mm), a compliant pure-aluminum interlayer (0.04 mm) and a lining of medium-strength aluminum alloy (0.38 mm). Previous experimental studies [1] with flat strip specimens of identical architecture under three point bendi...

Al~tract--The mechanics of fracture of a stably extending interface crack in polymeric adhesive bonds undergoing very large shear deformation is studied using a rate-del~ndent finite element analysis. Plane-strain and J2 plasticity conditions are considered. Based on recent experimental observations, it is assumed that the local engineering shear strain at a certain distance (i.e. for the polym...

the cracked brazilian disc (cbd) specimen is widely used in order to determine mode-i/ii and mixed-mode fracture toughness of a rock medium. in this study, the stress intensity factor (sif) on the crack-tip in this specimen is calculated for various geometrical crack conditions using the extended-finite element method (x-fem). this method is based upon the finite element method (fem). in this m...

A major part of fracture mechanics is concerned with studying the initiation and propagation of fatigue cracks. This typically requires constant monitoring of crack growth during fatigue cycles and the knowledge of the precise location of the crack tip at any given time. One technique currently available for measuring fatigue crack length is the Potential Drop method[1]. The method, however, ma...

Résumé. We study experimentally the paths of an assembly of cracks growing in interaction in a heterogeneous two-dimensional elastic brittle material submitted to uniaxial stress. For a given initial crack assembly geometry, we observe two types of crack path. The first one corresponds to a repulsion followed by an attraction on one end of the crack and a tip to tip attraction on the other end....