Thin film metallic glasses comprised of Zr48Cu36Al8Ag8 (at.%) of approximately 1.5 μm and 3 μm in thickness were prepared using magnetron sputtering onto medical grade 316L stainless steel. Their structural and mechanical properties, in vitro corrosion, and antimicrobial activity were analyzed. The amorphous thin film metallic glasses consisted of a single glassy phase, with an absence of any d...

This study investigates the effects of niobium and molybdenum on FeCoNi alloy, including on the microstructures and hardness of FeCoNiNb0.5Mo0.5 and FeCoNiNb alloys, and the polarization behaviors of these alloys in 1 M sulfuric acid and 1 M sodium chloride solutions. The results in this study indicate that both FeCoNiNb0.5Mo0.5 and FeCoNiNb alloys had a dual-phased dendritic microstructure; al...

The electrochemical corrosion behavior of NiTi alloy electrodeposited conductive polypyrrole (PPy) coatings doped with small size sulfate (SO42 ), medium size para-toluene sulfonate (pTS ) and large size dodecylbenzene sulfonate (DBS ) counter anions has been studied by electrochemical measurements and surface analysis. It is demonstrated that PPy coatings inhibit the corrosion of NiTi substrat...

PURPOSE The aim of this study was to evaluate the effects of repeated porcelain firing process on the corrosion rates of the dental alloys. MATERIALS AND METHODS Cr-Co, Cr-Ni and Pd-Ag alloys were used for this study. Each metal supported porcelain consisted of 30 specimens of 10 for 7, 9 and 11 firing each. Disc-shaped specimens 10 mm diameter and 3 mm thickness were formed by melting alloys...

The understanding of corrosion behavior in NiTi is critical for the devices using this shape-memory alloy. In order to improve the surface properties of NiTi such as corrosion resistance, plasma source ion implantation (PSII) technique was employed with oxygen as incident ions at three levels of implantation dose (5x10(16), 1x10(17) and 3x10(17) ions/cm(-2)). Pitting corrosion and wear-corrosio...

Hydroxyapatite (HA) has been used in clinical bone graft procedures for the past 25 years. Although a biocompatible material, its poor adhesion strength to substrate makes it unsuitable for major loadbearing devices. Investigations on various deposition techniques of HA coating on Ti–6Al–4V implants have been made over the years, in particular to improve its adhesion strength to the metal alloy...

New developments of antimicrobial implant surfaces doped with copper (Cu) ions may minimize the risk of implant-associated infections. However, experimental evaluation of the Cu release is influenced by various test parameters. The aim of our study was to evaluate the Cu release characteristics in vitro according to the storage fluid and surface roughness. Plasma immersion ion implantation of C...

The aims of this study were to investigate the effects of Zr addition and potentiodynamic polarization on the microstructure and corrosion resistance of Ti–22Nb and Ti–22Nb–6Zr alloy samples. The corrosion tests were carried out in 0.9% NaCl at 37 8C and neutral pH value, utilizing the OCP, potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) techniques.The results of ...

The aim of this study was to determine the effect of the oral environment on the corrosion of dental alloys with different compositions, using electrochemical methods. The corrosion rates were obtained from the current-potential curves and electrochemical impedance spectroscopy (EIS). The effect of artificial saliva on the corrosion of dental alloys was dependent on alloy composition. Dissoluti...

Composition modulated multilayer alloy (CMMA) coatings of Zn-Ni were electrodeposited galvanostatically on mild steel (MS) for enhanced corrosion protection using single bath technique. Successive layers of Zn-Ni alloys, having alternately different composition were obtained in nanometer scale by making the cathode current to cycle between two values, called cyclic cathode current densities (CC...