OBJECTIVES This study was performed to evaluate the cytotoxicity of four calcium silicate-based endodontic cements at different storage times after mixing. MATERIALS AND METHODS Capillary tubes were filled with Biodentine (Septodont), Calcium Enriched Mixture (CEM cement, BioniqueDent), Tech Biosealer Endo (Tech Biosealer) and ProRoot MTA (Dentsply Tulsa Dental). Empty tubes and tubes contain...

INTRODUCTION The purpose of this study was to evaluate the effect of different solvents; carbonic acid (H2CO3), hydrochloric acid (HCl), chlorhexidine (CHX) and sodium hypochlorite (NaOCl) on the surface hardness of mineral trioxide aggregate (MTA) and calcium-enriched mixture (CEM) cement. METHODS AND MATERIALS Plexiglass molds were prepared and filled with Angelus MTA or CEM cement and then...

OBJECTIVES To evaluate the outcome of vital pulp therapy in primary teeth with irreversible pulpitis by using calcium-enriched mixture (CEM) cement according to clinical and radiographic assessment. PARTICIPANTS AND METHODS Fifty primary molar teeth with irreversible pulpitis in 50 children aged 6-8 years underwent pulpotomy using CEM cement as the dressing material. Following pulpotomy, pain...

INTRODUCTION The aim of this in vitro study was to determine the sealing ability of orthograde ProRoot mineral trioxide aggregate (MTA) and calcium enriched mixture (CEM) cement as root-end filling materials. MATERIALS AND METHODS Fifty four extracted single-rooted human teeth were used. The samples were randomly divided into 3 experimental groups. In group A and B, 4 mm of WMTA and CEM cemen...

introduction: the aim of this in vitro study was to evaluate the effect of various irrigants on the push-out bond strength of calcium-enriched mixture (cem) cement and mineral trioxide aggregate (mta). methods and materials: a total of 140 dentin disks with a thickness of 1.5±0.2 mm and lumen size of 1.3 mm, were randomly divided into 12 groups ( n =10) and 4 control groups ( n =5). the lumen o...

introduction: the aim of this in vitro study was to evaluate the tooth discoloration induced by calcium-enriched mixture (cem) cement and mineral trioxide aggregate (mta). methods and materials: forty five endodontically treated human maxillary central incisors were selected and divided into three groups ( n =15) after removing the coronal 3 mm of the obturating materials. in the mta group, whi...

introduction: the purpose of this study was to compare the push-out bond strength of white proroot mineral trioxide aggregate (mta), biodentine, calcium-enriched mixture (cem) cement and endosequence root repair material (errm) putty after exposure to blood. methods and materials: a total of 96 root dentin slices with a standardized thickness of 1.00±0.05 mm and standardized canal spaces were r...

introduction: this in vitro study measured and compared ph and phosphate and calcium ions release of a new endodontic material (cem cement), mineral trioxide aggregate (mta), and portland cement (pc) using uv-visible technique, atomic absorption spectrophotometry methods, and ph meter, respectively. materials and methods: each material was placed in a plastic tube (n=10) and immersed in a glass...

background and aims. different materials have been used for root-end filling during surgical endodontic treatment. the aim of this in vitro study was to evaluate the dye penetration in different thicknesses of calcium enriched mixture (cem) cement as root-end filling material. materials and methods. following root canal filling in 70 extracted human single-rooted premolar teeth, the apical 3 mm...

introduction: sealing ability is an important factor for a root-end filling material in endodontic surgeries. this in vitro study aimed to compare the sealing ability of mineral trioxide aggregate (mta) and a new endodontic cement named calcium enriched mixture (cem) cement as root-end filling materials. materials and methods: the experiments were carried out in dry, saliva or blood contaminate...