By partitioning the total stresses in a damaged composite into either mechanical and residual stresses or into initial and perturbation stresses, it was possible to derive several exact results for the energy release rate due to crack growth. These general results automatically include the effects of residual stresses, traction-loaded cracks, and imperfect interfaces. The exact energy release r...

By partitioning the total stresses in a damaged composite into either mechanical and residual stresses or into initial and perturbation stresses, it was possible to derive several exact results for the energy release rate due to crack growth. These general results automatically include the effects of residual stresses, traction-loaded cracks, and imperfect interfaces. The exact energy release r...

Pulsed infrared laser irradiation was used to positively identify small fatigue cracks on the surface of fatigue damaged Ti–6Al–4V specimens. The resulting transient thermoelastic deformation perceptibly changes the opening of partially closed surface cracks without affecting other scatterers, such as surface grooves, corrosion pits, coarse grains, etc. that might hide the fatigue crack from ul...

BACKGROUND The role of peers (former or current drug users) in reducing risky behavior within methamphetamine and crack smokers has not been well described or researched. The current study not only explores the role of peers in reducing risk factors for morbidity within the illicit drug smoking population in the Downtown Eastside (DTES) community of Vancouver but it also investigates the change...

In this theoretical research work, the fracture characteristics of graphene-modified polymer nanocomposites were studied. A three-dimensional representative volume element-based multiscale model was developed in a finite element environment. Graphene sheets were modeled in an atomistic state, whereas the polymer matrix was modeled as a continuum. Van der Waals interactions between the matrix an...

X-ray absorption microtomography, a high resolution variant of medical “CT”, quantifies threedimensional microstructures efficiently and noninvasively. With this imaging modality, determination of the three-dimensional spatial distribution of crack opening as a function of applied load has helped clarify important physical processes of roughness-induced fatigue crack closure. There is a real ne...

In previous work, fatigue-crack-growth tests were conducted on middle-crack tension, M(T), and compact, C(T), specimens made from the same D16Cz (clad) aluminum alloy sheet. These tests were conducted over a wide range of stress ratios (R = Pmin/Pmax = 0.5 to 0.75) to generate crack-growth-rate data from threshold to near fracture. These tests were used to generate the effective stress-intensit...

In-situ synchrotron X-ray microtomography has been employed to investigate the three-dimensional (3D) closure behavior of short fatigue crack in Ti-6Al-4V alloy. At a spatial resolution level 1 µm, tomography datasets were taken at two fronts observe time evolution (sometimes called 4D imaging). Owing high level, complex 3D morphology consisting deflections, facet paths and branching/overlap ca...

An extension of the celebrated Paris law for crack propagation is given to take into account some of the deviations from the power-law regime in a simple manner using the Wöhler SN curve of the material, suggesting a more general ‘‘unified law’’. In particular, using recent proposals by the first author, the stress intensity factor K(a) is replaced with a suitable mean over a material/structura...

OBJECTIVE This is a report of 50 consecutive patients with juxtapyloric perforations after smoking "crack" cocaine (cocaine base) at one urban public hospital. SUMMARY BACKGROUND DATA Although the exact causal relation between smoking crack cocaine and a subsequent juxtapyloric perforation has not been defined, surgical services in urban public hospitals now treat significant numbers of male ...