Fatigue crack growth behavior of AZ61 magnesium alloy was investigated in low humidity (55% relative humidity) and 3.5% NaCl spray environments under various stress ratios. Fatigue crack growth rates became higher with increasing load ratio for both environments. However, the results of fatigue crack growth test under 3.5% NaCl spray environment showed lower fatigue crack propagation rate compa...

An evaluation of the fatigue crack resistance of human dentin was conducted to identify the degree of degradation that arises with aging and the dependency on tubule orientation. Fatigue crack growth was achieved in specimens of coronal dentin through application of Mode I cyclic loading and over clinically relevant lengths (0 ≤ a ≤ 2 mm). The study considered two directions of cyclic crack gro...

An infinite elastic medium with a planar crack is considered. The crack is subjected to the pressure of fluid injected at a point on the crack surface. Description of the crack growth is based on the lubrication equation (balance of the injected fluid and the crack volume), the equation for crack opening caused by fluid pressure on the crack surface, the Poiseuille equation related local fluid ...

concrete is one of the most widely used materials in construction industry. many large and important structures such as power plants, bridges, dams and buildings employ concrete as main material. propagation of crack is considered one of the main reasons in failure of concrete structures. the process of formation and crack growth is one of the major and complex issues in concrete, because concr...

The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy 2024 was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact su...

The inspection of various structures often detects a fatigue cracks developed during long service life. These fatigue cracks significantly reduce remaining fatigue life and fatigue strength. Influence of the initial fatigue cracks size in non-load-carrying fillet-welded one-sided transverse attachment joints on the remaining fatigue life and fatigue strength is considered in this paper. A compu...

Recent theoretical results on elastic-plastic planestrain crack growth an~ reviewed and experimental results for crack growth in a 4140 steel are discussed in terms of the theoretical concepts. The theory is based on a recent asymptotic analysis of crack surface opening and strain distributions at a quasistatically advancing crack tip in an ideally plastic solid. The analysis is incomplete in t...

Axial loading tests with stress ratios R of -1, 0 and 0.3 were performed to examine the fatigue failure behavior of a carburized Cr-Ni steel in the long-life regime from 10⁴ to 10⁸ cycles. Results show that this steel represents continuously descending S-N characteristics with interior inclusion-induced failure under R = -1, whereas it shows duplex S-N characteristics with surface defect-induce...