In the present study, friction spot welding or refill friction stir spot welding was performed to consolidate dissimilar AA5754 Al and AZ31 Mg alloys. The intermetallic compounds of Al12Mg17 and Al3Mg2 were primarily found in the weld, distributed at the interface between the base materials and in the Al top sheet. The distribution of the intermetallic compounds and the interfacial area between...

The debonding behaviour of fibres strongly affects the properties of fibre-reinforced composites. In the literature, two different approaches to the fibre debonding problem have been developed. In strength-based approaches [1-4], interracial debonding is assumed to occur once an interfacial strength is reached. In fracture-based approaches [5-9], the debonded interfacial zone is regarded as a t...

Although cement-within-cement revision arthroplasty minimizes the complications associated with removal of secure PMMA, failure at the interfacial region between new and old cement mantles remains a theoretical concern. This article assesses the variability in shear properties of bilaminar cement mantles related to duration of postcure and the use of antibiotic cements. Bilaminar cement mantles...

The properties of the fiber/matrix interface in composites have an influence on their overall performance. Common methods for studying the interface are micromechanical tests that load a single fiber/matrix interface to failure. Two popular tests are the microbond test [1] and the single-fiber, pull-out test [2]. In a microbond test a droplet of matrix is sheared off the fiber by pulling the fi...

Magnetically soft/hard exchange-coupled Ni80Fe20 /Si3N4 /Sm40Fe60 and Ni80Fe20 /mixture/ Sm40Fe60 layered structures with induced in-plane uniaxial anisotropy were deposited by sputtering on Si ~100! substrates. The interfacial exchange coupling strength between the soft and hard layers was tailored by inserting a thin nonmagnetic insulating Si3N4 layer or by varying interfacial mixture of NiFe...

Effects of reflow time on the interfacial microstructure and shear strength of the SAC/FeNi-Cu connections were investigated. It was found that the amount of Cu6Sn5 within the solder did not have a noticeable increase after a long time period of reflowing, indicating that the electro-deposited FeNi layer blocked the Cu atoms effectively into the solder area during a long period under liquid-con...

For adhering to three-dimensional (3D) surfaces or objects, current adhesion systems are limited by a fundamental trade-off between 3D surface conformability and high adhesion strength. This limitation arises from the need for a soft, mechanically compliant interface, which enables conformability to nonflat and irregularly shaped surfaces but significantly reduces the interfacial fracture stren...

This study compared the fluid filtration, adaptation to the root canal walls, and the push-out bond strength of two resin-based sealers and three calcium silicate-based retrograde filling materials. Fifty maxillary canines were shaped using manual instruments and the apical portion was sectioned. Retrograde cavities of 3-mm depth were prepared. The specimens were divided into five groups (n = 1...

The influence of chemical cleaning agents on the bond strength between resin cement and glass-fiber posts was investigated. The treatments included 10% hydrofluoric acid, 35% phosphoric acid, 50% hydrogen peroxide, acetone, dichloromethane, ethanol, isopropanol, and tetrahydrofuran. Flat glass-fiber epoxy substrates were exposed to the cleaners for 60 s. Resin cement cylinders were formed on th...