Friction and wear tests were performed on AISI 1045 steel specimens with different initial roughness parameters, machined by a creep-feed dry grinding process, to study the friction and wear behavior on a pin-on-disc tester in dry sliding conditions. Average surface roughness (Ra), root mean square (Rq), skewness (Rsk) and kurtosis (Rku) were involved in order to analyse the influence of the fr...

In the present study, enamel wear against indirect composite resins was evaluated using two newly designed wear test methods: a rotating sliding wear test and a buff wear test. For the composite resins investigated in this study, their surface morphologies were examined using a scanning probe microscope after buff-polishing. After the wear tests, enamel was worn down by hard fillers that protru...

The authors report tribochemical changes due to sliding of a silicon nitride Si3N4 ball against an ultrananocrystalline diamond UNCD thin film. Unidirectional sliding wear measurements were conducted for 2000 cycles using a ball-on-disk apparatus with a 3/16 in. diameter Si3N4 ball at a sliding speed of 3.3 mm/s and a normal load of 98.0 mN nominal Hertzian stress of 0.6 GPa in a nitrogen envir...

The tribological behaviour of anodic oxide layer formed on Al5754, used in automotive applications, was investigated against test parameters. The friction coefficient under different normal loads, sliding speeds, and oxide thicknesses was studied using a pin on disc tribometer. Results show that the increase of load and sliding speed increase the friction coefficient. The rise of contact pressu...

This paper comparatively studies the tribological behaviour of different types of diamond-like carbon (DLC) coatings in a reciprocating sliding wear test. The results are interpreted in terms of structure and surface morphological characteristics. At the beginning of each reciprocating sliding wear test, the higher coefficient of friction of the DLC coatings reflects the original surface condit...

Friction coefficient and wear rate of different steel materials are investigated and compared in this study. In order to do so, a pin on disc apparatus is designed and fabricated. Experiments are carried out when different types of disc materials such as stainless steel 314 (SS 314), stainless steel 202 (SS 202) and mild steel slide against stainless steel 314 (SS 314) pin. Experiments are cond...

Simultaneous measurements of the curves for wear versus distance, wear rate versus distance, and coefficient of friction versus distance were performed in situ to distinguish the transition from severe running-in wear to mild wear. The effects of the initial surface roughness on the severe running-in wear volume were investigated. Disk-on-plate friction and wear tests were carried out with SUS3...

After the gamma-irradiation sterilization, the most widely used orthopaedic grade polymer bearing liner material for the total joint replacement, ultra-high molecular weight polyethylene (UHMWPE), degrades through the progressive in vivo oxidation. The oxidative degradation makes UHMWPE brittle and leads to reduction of its mechanical properties. In this study, the effect of the in vivo post-ir...

An investigation of the friction and sliding wear of gray cast iron against chromium plated cast irons was carried out on a newly constructed reciprocating friction and wear tester. The tests were the first to be done on the test rig under dry conditions and at the speed of 170 cm/min, and variable loads of 20-260 N for a duration of 15 min. to 3 hours. The gray cast iron surfaces worn by a pro...

A 16-station wear simulator of the pin-on-disc type, called RandomPOD, was designed, built, and validated. The primary area of application of the RandomPOD is wear studies of orthopaedic biomaterials. The type of relative motion between the bearing surfaces, generally illustrated as shapes of slide tracks, has been found to have a strong effect on the type and amount of wear produced. The compu...