This paper reviews the dependence of strength and fatigue of fused silica optical fiber on the environmental parameters temperature, humidity and pH. It is shown that the stress corrosion parameter, n, is not a constant but depends on the nature of the environment. Further, different kinetic forms for the stress corrosion kinetics lead to different interpretations of experimental results. Since...

Detection of Metal Defects on Gas Distribution Pipeline by Remote Field Eddy Current (RFEC) Using Finite-Element Analysis — It is necessary to find out whether there are metal defects on underground gas distribution pipelines without excavation in order to establish safety strategies for replacement or maintenance. The metal defects are classified into general corrosion, stress corrosion cracki...

There are a number of ways to improve the corrosion and abrasion resistance of metals, including alloying, anodizing, nitriding and application of protective thin films. Alloying involves generating a binary phase diagram to determine the optimum composition and temperature dependence. For example, copper alloys known as “bronzes” offer high strength, abrasion resistance and high temperature co...

An overview is given of the anomalous behavior of some metals, in particular Fe and Cr, in acidic aqueous solutions during anodic dissolution. The anomaly is recognizable by the fact that during anodic dissolution more material dissolves than would be expected from the Faraday law with the use of the expected valence of the formed ions. Mechanical disintegration, gas bubble blocking, hydrogen e...

Chemical process installations are exposed to aggressive chemicals and conditions leading to corrosion. The damage from corrosion can lead to an unexpected plant shutdown and to the exposure of people and the environment to chemicals. Due to changes within and on the surface of materials subjected to corrosion, energy is released in the form of acoustic waves. This acoustic activity can be capt...

The effect of Cr(VI) pollution on the corrosion rate of corrugated iron roof samples collected from tanning industry areas was investigated through simulated laboratory exposure and spectrophotometric detection of Cr(III) deposit as a product of the reaction. The total level of Cr detected in the samples ranged from 113.892 ± 0.17 ppm to 53.05 ± 0.243 ppm and showed increasing trend as sampling...

Government nor any agency thereof, nor any of their employees, makes any warranty, express or implied, or assumes any legal liability or responsibility for the accuracy, completeness, or usefulness of any information, apparatus, product or process disclosed, or represents that its use would not infringe privately owned rights. Reference herein to any specific commercial product, process or serv...

Linearly Increasing Stress Tests conducted in 30 C aerated distilled water using as-quenched 4340 and 3.5NiCrMoV turbine rotor steels indicated that stress corrosion cracking occurred at all applied stress rates for 4340 steel, whilst only at applied stress rates less than or equal to 0.002 MPa s 1 for the turbine rotor steel. The crack velocity increased with increasing applied stress rate for...

UNLABELLED NiTi spring coils were used to obtain large deformation under a constant force. The device consists on a NiTi coil spring, superelastic at body temperature, in order to have a stress plateau during the austenitic retransformation during the unloading. The temperature variations induced changes in the spring force. OBJECTIVES The aim of this study is to investigate the effect of the...