In this paper, an experimental investigation on ultrasonic welding of polyamide composites reinforced with glass fiber has been carried out. The effect of ultrasonic welding parameters, such as welding time, air pressure, hold time and the amount of glass fiber in the composite on tensile strength of weld joints were determined using response surface methodology. This methodology was applied fo...

In the present research work, the flexural modulus and strength of glass fiber-epoxy resin and carbon fiber-epoxy resin composites have been enhanced through fiber tension during curing of the polymeric resin. This study showed that the tension applied on the fibers increased the flexural modulus of the glass-epoxy composites up to 12% and the flexural strength up to 19%. The flexural modulus a...

Glass fiber-reinforced endodontic posts are considered to have favorable mechanical properties for the reconstruction of endodontically treated teeth. The aim of the present investigation was to evaluate the survival of two tapered and one parallel-sided glass fiber-reinforced endodontic post systems in teeth with different stages of hard tissue loss and to identify risk factors for restoration...

OBJECTIVE Contradictory results have been reported over microleakage studies of restorative materials and methods. Despite the number of publications on leakage there are few evidences comparing the different microleakage evaluation methods. The purpose of the present study was to compare the clearing technique and longitudinal sectioning in the evaluation of dye penetration along a glass fiber...

Background Fiber reinforced composite (FRC) is a promising class of material that gives clinicians alternative treatment options. There are many FRC products available in the market based on either glass or polyethylene fiber type. The aim of this study was to present a comparison between glass and polyethylene fiber reinforced composites based on available literature review. Material and Met...

Background and aim: Studies as to the evaluation of clinically relevant color assessment of full ceramic restorations supported by esthetic post and core materials has not been found in the related literature. Thus, this study is conducted to evaluate the color difference of Empress 2 ceramic crowns restored with 4 different esthetic post systems and two different core materials by using colori...

PURPOSE To compare the fracture resistance and the mode of failure of endodontically treated teeth restored with different post-core systems. MATERIALS AND METHODS Root canal treatment was performed on 40 maxillary incisors and the samples were divided into four groups of 10 each. For three experimental groups post space preparation was done and teeth were restored with cast post-core (Group ...

objective: there is no definitive data on the strength of glass fiber and cast posts with different length. this in vitro study was designed to investigate and compare the effect of length on the retentive strength of glass fiber and cast posts. materials and methods: sixty recently extracted intact maxillary canine teeth were cut 1mm above the cej. the specimens were endodontically treated and...

background: with the aim of developing methods that could increase the fracture resistance of structurally compromised endodontically treated teeth, this study was conducted to compare the effect of three esthetic post systems on the fracture resistance and failure modes of structurally compromised and normal roots. materials and methods: forty five extracted and endodontically treated maxillar...

Using three-dimensional finite element analysis (3D-FEA), stress distributions in the remaining radicular tooth structure were investigated under the condition of varying diameters of fiber post for fiber post-reinforced composite resin cores (fiber post and core) in maxillary central incisors. Four 3D-FEA models were constructed: (1) fiber post (ø1.2, ø1.4, and ø1.6 mm) and composite resin cor...