y-tial intermetallic alloy have a good potential for use as biomaterial, due to its good corrosion resistance. in this paper, two fundamental electrochemical techniques namely electrochemical impedance spectroscopy and potentiodynamic anodic polarization were used to evaluate the corrosion performance of g-tial in ringer's solution. surface modification treatments were employed with the pu...

Previous studies showed that temperature and total organic carbon in drinking water would cause chlorine dioxide (ClO(2)) loss in a water distribution system and affect the efficiency of ClO(2) for Legionella control. However, among the various causes of ClO(2) loss in a drinking water distribution system, the loss of disinfectant due to the reaction with corrosion scales has not been studied i...

The effect of Cr(VI) pollution on the corrosion rate of corrugated iron roof samples collected from tanning industry areas was investigated through simulated laboratory exposure and spectrophotometric detection of Cr(III) deposit as a product of the reaction. The total level of Cr detected in the samples ranged from 113.892 ± 0.17 ppm to 53.05 ± 0.243 ppm and showed increasing trend as sampling...

Problem statement: This study showed the results of an experimental investigation on the strengthening of corrosion damaged reinforced concrete beams with unidirectional cloth glass fiber reinforced polymer (UDCGFRP) laminates. Approach: All the beam specimens 150×250×3000 mm were cast and tested for the present investigation. One beam specimen was neither corroded nor strengthened to serve as ...

OBJECTIVES The aim of the present study was to investigate the effect of thermal oxidation on the corrosion behavior of Ti-5Ag alloy. METHODS The microstructure of Ti-5Ag alloy without and with thermal oxidization treatment were characterized, with commercial pure (CP) Ti as control, by means of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (...

We have developed a concrete material exhibiting self-healing properties and corrosion inhibition. This system involves a sodium silicate solution stored in polyurethane microcapsules present in the concrete matrix. The sodium silicate, released when the capsules are ruptured by propagating cracks, reacts with the calcium hydroxide in cement and produces a C-S-H gel that partially heals the cra...

Five non-precious Ni-Co based alloys were analyzed with respect to their corrosion behaviour. The correlation between the amount of the elements Cr, Mo, V and the corrosion behaviour, expressed by the PREN (pitting resistance equivalent number) index in the case of the allied steels, was extended for Ni-Cr and Co-Cr dental alloys characterization. Open circuit potential, corrosion current densi...

An innovative sensor containing A36 carbon steel was explored for corrosion monitoring. After being soaked in an aerated 0.2 M NaCl solution, the sensor’s normalized electrical resistance (R/R0) decreased continuously with the extent of corrosion from 1 to 0.64. Meanwhile, the sensor’s normalized capacitance (C/C0) increased continuously from 1.0 to 1.42. The sensors can be attached to a struct...

A TCP–TCL model is established to describe the relationship between the thickness of the corrosion-filled paste (CP) and that of the corrosion layer (CL). This model can describe the phenomenon that the corrosion filling in the concrete pores and accumulating at the steel/concrete interface occur synchronously. Based on the TCP–TCL model, a corrosion-induced concrete cracking model, which can q...

The self-assembled monolayer (SAM) was prepared using octadecyl trichlorosilane (OTS) in distilled solution on the copper surface. The effect of inhibitor concentration on the rate of inhibition efficiency and corrosion rate in corrosion medium on copper by using polarization curves, electrochemical impedance spectroscopy (EIS), scanning electron microscope (SEM) was studied. The results showed...