In this study, AISI 1020 steel surface was coated in different heat inputs with (wt.-%) 50FeCrC-20FeW-30FeB powder mixture by using plasma transferred arc (PTA) welding method. The microstructure of the coated samples were investigated by using optical microscope (OM), scanning electron microscope (SEM), X-ray diffraction (XRD) and energy dispersive X-ray (EDS). The hardness was measured with m...

The tough bulk of dentin in teeth supports enamel, creating cutting and grinding biostructures with superior failure resistance that is not fully understood. Synchrotron-based diffraction methods, utilizing micro- and nanofocused X-ray beams, reveal that the nm-sized mineral particles aligned with collagen are precompressed and that the residual strains vanish upon mild annealing. We show the l...

the development of nano/ultrafine bainitic structure in aisi 52100 steel was the goal of this study. for this purpose,the aisi 52100 the specimens were austenitized at 1050 °c for 60 min followed by low-temperature austemperingtreatment at different temperatures and times. the austempered samples were characterized using field emissionscanning electron microscopy (fesem), x-ray diffraction (xrd...

development of an eco-friendly, low cost and high energy density limnpo4 cathode material has attracted much attention due to its high operating voltage vs. li falling within the electrochemical stability window of conventional electrolyte solutions and offers more safety features due to the presence of a strong p-o covalent bond.synthesis of battery materials integrates the battery technology ...

a new approach for the synthesis of prussian blue nanoparticles using the cationic surfactant cetyl pyridinium chloride (cpc) as capping agent has been developed in the present work. powder x-ray diffraction, transmission electron microscopy, uv–vis absorption spectra, and ir spectroscopy were employed to characterize the product. the tem image showed that the prussian blue nanoparticles with d...

the preparation of nano-sized tio2 by titanium tetraisopropoxide (ti(oipr)4) via sol-gelmethod using acid as a catalyst is investigated and the optimized conditions concerning theproportional amount of acid, water, alcohol is established by xrd and sem. the effect ofcalcination temperature on phase transformation of tio2 (rutile, anatase and brookite) wasdetermined by xrd. the smallest grain si...

nanocrystalline hydroxyapatite was precipitated from calcium hydroxide and phosphoric acid. effects of precipitation temperature and different calcium to phosphate ratios (ca/p) on the obtained powders were investigated. characteriza-tion of the powders was performed using xrd and ftir spectra, scanning electron microscopy, and transmission electron microscopy. increase in precipitation tempera...

X-ray diffraction, optical microscopy and microhardness testing have been used to study properties which develop in micro-cut AISI 1045 steel. The influence of the ploughing effect on residual stresses, surface deformation and work hardening, and the tool quality were investigated. Tensile residual stresses, caused by the heat generated in the material during the cutting process, were observed ...

The arsenic (As) solid-state speciation (i.e., oxidation state, precipitates, and adsorption complexes) is one of the most important factors controlling dissolved As concentrations at As contaminated sites. In this case study, two representative subsurface samples (i.e., oxidized and semi-reduced sites) from former lead arsenate contaminated soils in the northeastern United States were chosen t...

The monochromator and focusing mirrors of the 16-BM-D beamline, which is dedicated to high-pressure research with micro-X-ray diffraction (micro-XRD) and X-ray absorption near edge structure (XANES) (6-45 keV) spectroscopy, have been recently upgraded. Monochromatic X-rays are selected by a Si (111) double-crystal monochromator operated in an artificial channel-cut mode and focused to 5 μm × 5 ...