OBJECTIVES The objective of this in vitro study was to evaluate the fatigue crack growth properties of the dentin/resin adhesive interface. METHODS Compact tension (CT) specimens were prepared from coronal dentin, resin composite, and dentin bonded to resin composite using Optibond Solo Plus adhesive. All specimens were then subjected to cyclic Mode I loading while fully hydrated at a stress ...

Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...

An understanding of how fatigue cracks grow in bone is of importance as fatigue is thought to be the main cause of clinical stress fractures. This study presents new results on the fatigue-crack growth behavior of small surface cracks (approximately 75-1000 microm in size) in human cortical bone, and compares their growth rates with data from other published studies on the behavior of both surf...

in this paper, three-dimensional modeling of the fatigue crack growth profiles was performed in a simple riveted lap joint. simulation results showed that mode i was dominated on the one side of the plates and the crack straightly grew on this side, while the other side of the plates was in a mixed-mode condition and the crack propagation path was not straight on this side. afterward, the fract...

An electromagnetic NDE technique for measuring the crack ooening displacement of surface fatigue cracks is described. A ferromagnetic resonance probe utilizing yttrium-iron-garnet was used to induce eddy currents in an aluminum plate. The crack opening disolacement of a semi-elliptical fatigue crack evaluated at the surface was measured optically at several values of bending stress on the speci...

This paper presents a new incremental formulation for predicting the curved growth paths of twodimensional fatigue cracks. The displacement and traction boundary integral equations (BIEs) are employed to calculate responses of a linear elastic cracked body. The Paris law and the principle of local symmetry are adopted for defining the growth rate and direction of a fatigue crack, respectively. ...

A B S T R A C T Effect of microstructure on mixed-mode (mode I ‡ II), high-cycle fatigue thresholds in a Ti-6Al-4V alloy is reported over a range of crack sizes from tens of micrometers to in excess of several millimeters. Specifically, two microstructural conditions were exam-inedÐa fine-grained equiaxed bimodal structure (grain size $20 mm) and a coarser lamellar structure (colony size $500 m...

The high-cycle, push-pull fatigue fracture behavior of high-C, Si-Al-rich nanostructured bainitic steel was studied through the measurement of fatigue limits, a morphology examination and phase composition analysis of the fatigue fracture surface, as well as fractography of the fatigue crack propagation. The results demonstrated that the push-pull fatigue limits at 10⁷ cycles were estimated as ...

In previous work, fatigue-crack-growth tests were conducted on middle-crack tension, M(T), and compact, C(T), specimens made from the same D16Cz (clad) aluminum alloy sheet. These tests were conducted over a wide range of stress ratios (R = Pmin/Pmax = 0.5 to 0.75) to generate crack-growth-rate data from threshold to near fracture. These tests were used to generate the effective stress-intensit...

Fatigue is the major threat in service of steel structure subjected to fluctuating loads. With the additional effect of corrosion and presence of weld joints the fatigue failure may become more critical in structural steel. One of the apt examples of such structural is the sailing ship. This is experiencing a constant stress due to floating and a pulsating bending load due to the waves. This pa...