Significant stress concentrations in welded structures typically arise at crack like defects and at weld toes. The geometry of the weld toe is therefore one of the primary geometrical features that control the fatigue life of welded components. This work is focused on evaluating three non-destructive methods to measure the weld toe radius: Weld Impression Analysis (WIA), Laser Scanning Profilin...

Tailor-welded blanks (TWB) are blanks with sheets of similar or dissimilar thicknesses, materials, coatings welded in a single plane before forming. Applications of TWB include car door inner panel, deck lids, bumper, side frame rails etc. in automotive sector (Kusuda et al., 1997; Pallet & Lark, 2001). Aluminium TWBs are widely used in automotive industries because of their great benefits in r...

As is well known that sensing and measuring the weld pool surface is very important to design intelligent welding machines which is able to imitate a skilled human welder who can choose suitable welding parameters. Therefore, in this paper, we concentrate the problem of weld pool surface 3D reconstruction, which is a key issue in intelligent welding machines development. Firstly, the framework ...

Characterization of flaws of weld bead is imperative for high-quality welding. Methods of weld bead inspection include radiographic, ultrasonic and vision inspection. However, such methods are costly and time consuming. The proposed sensor is light, low-cost and fast. This paper summarizes our work on weld bead monitoring and defect detection using an electromagnetic sensor. Measurements are ac...

This paper investigates the development of weld zone in Resistance Spot Welding (RSW) which focuses on weld nugget and Heat Affected Zone (HAZ). The effects of four factors namely weld current, weld time, electrode force and hold time were studied using a general 2 factorial design augmented by five centre points. The results of the analysis showed that all selected factors except hold time exh...

Acoustic Emission (AE) Technique is the only Non Destructive Testing (NDT) method that can be thought of to be used as an online monitoring tool for detection, location and characterization of various kinds of active defects during any process. An effective approach of quality control is defect detection during welding process itself rather than by NDT of component after welding. Weld defects g...

Fatigue crack growth observed in tubular K-joint specimens, typical of tubular bridge structures, always initiates at the chord crown toe locations whether the applied stress range is tensile or compressive. Even though other locations around the weld have highest hot-spot stresses, chord crown toe locations are still the most critical. This raises the question about the relevant tensile residu...

Welded joints of dissimilar steels are widely used in various components the steam-water circuit at thermal and nuclear power plants. In such welded after tempering during high-temperature operations, carbon migrates through fusion surface from less alloyed steel to more due difference chemical potential these steels. Decarburization weld-adjacent area ​​the heat affected zone steel, which occu...

The level of residual stresses generated in fusion welds has been a major area of interest for many years. For steels, a major influence on the final state of stress is through martensitic transformation. This is because the martensitic transformation is accompanied by significant shear and volume strains. One way to mitigate the development of residual stress is by controlling the onset of the...

In this Part II, a thorough investigation of the melting of the electrode; the droplet formation, detachment, transfer and impingement onto the workpiece, and the weld-pool formation and dynamics was conducted. The transient melt-flow velocity and temperature distributions in the droplet and in the weld pool were calculated. The resulting crater in the weld pool and the weld-pool oscillation du...