in this work, sol-gel processing was used to synthesize the fluorohydroxyapatite (nano-fha, ca10(po4)6(oh)2−xfx) nanopowders. the advantages of the sol-gel method over other methods are precise control of composition, low processing temperature, and better homogeneity. calcium nitrate tetrahydrate, phosphorous pentoxide and tetrabuthylammonium fluoride were used, respectively, as p, ca, and f p...

the aim of this study is to evaluate the influence of ph on the synthesis of nanocrystallines cobalt ferrite by combination of sol- gel auto combustion and ultrasonic irradiation methods. two different fuels, urea and thiourea, along with metal nitrates (oxidant) were used to prepare cofe2o4 powders. the morphology of the resulting powders was investigated. the powders were characterized by x-r...

ZnGa2O4 nano crystals were prepared by an improved coprecipitation method, which we call ‘spray coprecipitation’. XRD results shows the resulting crystal size using the new method is under 10nm, whereas the powder prepared by ordinary coprecipitation is about 30nm. XRD results also shows ZnO peaks exists in ZnGa2O4 powder prepared by traditional coprecipitation, but disappears in ZnGa2O4 nano c...

A new organogelator, benzyl (4-methyl-1-oxo-1-(2-hexadecanoylhydrazinyl)pentan-2-yl)carbamate (designated as Cbz-Leu-HdHz), was designed and synthesized, which could self-assemble in many organic solvents and form the thermally reversible physical supramolecular organogels. The gel-sol phase transition temperatures (TGS) were determined as a function of gelator concentration and the correspondi...

In the present endeavour, SnO2 nanoparticles (NPs) were synthesized using microwave method. Synthesized SnO2 NPs were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectrscopy (EDS) to find their structure, morphology and elemental composition. SnO2 NPs were of spherical morphology having crystallite size of 35.42 nm as obtained from Scher...

The aim of the current work is the synthesis and characterization of metallic Zr nanoparticles. The preparation is carried out by using the RAPET method (Reaction under Autogenic Pressure at Elevated Temperatures) developed in our lab. The RAPET reaction of commercial ZrO(2) with Mg powder was carried out in a closed stainless steel cell, at 750 °C. On completion of the reaction, the additional...

Silane modified iron (III) oxide (SiFe2O3) nanoparticles reinforced chitosan (CS) nanocomposite membranes were prepared by solcast transformation method. The iron (III) oxide nanoparticles and nanocomposite membranes were investigated by UV (Visible) spectroscopy, FT-IR spectroscopy, XRD, SEM and TEM. The size and shape of iron (III) oxide and Si-Fe2O3 nanoparticles were determined by XRD and T...

Zinc Oxide doped with chromium and cobalt, in form of powder with nanometer size has been prepared by typical solgel route, with assistance of microwave radiations. The as prepared material’s structure was characterized under XRays Diffraction(XRD) and Scherrer formula was used to find the crystal size. The materials also have been characterized under Scanning Electron Microscope(SEM) and Trans...

A hydrothermal method of synthesizing hydroxyapatite by heating a precipitate, formed by mixing Ca(NO3)2⋅4H2O and (NH4)2HPO4 with distilled water, in a hydrothermal reactor at 200 C for 24-72 hrs is described. A treatment time of 24 hrs produced single phase (as shown by XRD) hydroxyapatite powder, however for longer treatment times XRD patterns were indicative of the presence of a secondary ph...

Nanostructured cadmium oxide (CdO) films were fabricated on glass substrates from alkaline baths containing saccharin as an additive by a successive ionic layer adsorption and reaction (SILAR) method. The effects of saccharin concentration in the bath on the structural, morphological, and optical properties were studied by means of scanning electron microscopy (SEM), X-ray diffraction (XRD), ph...