We investigated the effects of hygrothermal aging on the tension–tension fatigue behavior of unidirectional (UD) glass/polydicyclopentadiene (pDCPD) composites. Samples were immersed in deionized (DI) water and salt water, and glass/epoxy composites were used as a benchmark for comparison. Composites of pDCPD showed less water uptake and superior fatigue performance compared to similarly aged e...

Mechanical properties of hybrid braided composite rebars are evaluated and compared to theoretical predictions which account for specific processing parameters including yarn size, braiding machine setup, and fiber type. Using a combination of high modulus carbon (Thornel P-55S) and aramid (Kevlar 49) fibers bars have been produced of up to 10 mm diameter with a Young's modulus of 200 GPa, a bi...

Micro-sized Al2O3-modified carbon fiber hybrid reinforced polymer composites (CFHRP) were prepared using the vacuum-assisted resin transfer molding (VARTM) process, and friction wear tests performed on an MRTR-1 multifunctional tester to study effect of surface doping with trace amounts Al2O3 its content tribological properties composites. The morphology composite material was characterized a t...

Interlaminar shear strength (ILSS) of fiber reinforced polymer composite is an important property for most of the structural applications. Matrix modification is an effective method used to improve the interlaminar shear strength of composite. In this paper, EPON 862/w epoxy system was modified using Tetraethyl orthosilicate (TEOS) electrospun nanofibers (ENFs) which were produced using electro...

PURPOSE To evaluate the effects of hydrogen peroxide pretreatment and heat activation of silane on the shear bond strength of fiber-reinforced composite posts to resin cement. MATERIALS AND METHODS The specimens were prepared to evaluate the bond strength of epoxy resin-based fiber posts (D.T. Light-Post) to dual-curing resin cement (RelyX U200). The specimens were divided into four groups (n...

The modification of carbon fibers for improving adhesion between fibers and an epoxy resin in composite materials has become the focus of attention. In this work the carbon fiber coating process has been devised in a way preventing the stiffening and clumping of fibers. To improve interactions between coated fibers and a resin in composites, four types of silica coatings with different organic ...

Epoxy – Polysulfide copolymers without or with low amounts of epoxy in their structure have poor mechanical properties in oxidative curing system.To strengthen the mechanical properties of polysulfide elastomer inclusion of epoxy resin (Epon828) as hard segment was studied. FT-IR spectroscopy and rheometry were used to verify the formation of epoxy-polysulfide copolymer.  Results obtained f...

A cationic photo-curable cycloaliphatic epoxy resin has been investigated as reactive monomer in blue light crosslinking process. We have demonstrated that camphorquinone is able to abstract labile hydrogen from the epoxy monomer, giving rise to the formation of carbon-centered radicals that are oxidized by the onium salt; a complete epoxy group conversion was reached after 50 s of irradiation....

To improve the thermal and mechanical properties of epoxy resins, epoxy-functionalized POSS (E-POSS) glass fiber (GF) were used to reinforce resin (E51) composites. The tensile, thermo-mechanical, fractured, tests carried out characterize these hybrid materials. results show that E-POSS GF could significantly resins due high crosslink density matrix synergistic interaction between resin, E-POSS...