In this study, dimmer-acid-based hybrid nonisocyanate polyurethanes (HNIPUs) were synthesized by the one-step method without catalyst. Three polyamines and two epoxy resins were selected as raw materials for HNIPU, and cyclic carbonate was synthesized based on our previous work. All of the products were characterized by Fourier transform infrared spectroscopy (FTIR), differential scanning calor...

Extrusion freeform fabrication has been used to make bars of fiber-reinforced epoxidized soybean oil (ESO)/epoxy resin. Freeform fabrication methods build materials by the repetitive addition of thin layers. The mixture of epoxidized soybean oil (ESO) and epoxy resin are modified with a gelling agent to solidify the materials until curing occurs. The high strength and stiffness composites are f...

In this study, acrylated soybean oil (AESO) was used as modifying agent for DGEBF-type epoxy resin (ER). AESO was used as a co-matrix in 50 wt % with ER. Composites with ecofriendly natural fillers-banana bark and seashell were prepared. MNA was used as a hardener. Effect of banana peel (BP) and seashell (SSh) fillers on mechanical properties, such as tensile strength, elongation at break, and ...

The curing reaction of a commercial cold-curing structural epoxy resin, specifically formulated for civil engineering applications, was analyzed by thermal analysis as a function of the curing time and the sample thickness. Original and remarkable results regarding the effects of curing time on the glass transition temperature and on the residual heat of reaction of the cold-cured epoxy were ob...

In this paper, the rheological behaviour of a petroleum-based epoxy (EL2 laminating epoxy) was compared with Super Sap CLR clear bio-resin epoxy. The focus work on viscous and viscoelastic performance these resins. Rheological tests were carried out at 15, 30, 60 min after mixing pure epoxies hardeners constant temperature 25 °C. results obtained from rheometer showed that viscosity both system...

Despite several excellent properties including low shrinkage, good chemical resistance, curable at low temperatures and the absence of byproducts or volatiles, epoxy resins are susceptible to ultra violet (UV) damage and their durability is reduced substantially when exposed to outdoor environments. To overcome this drawback, UV absorbers have been usually used to decrease the rate of UV degrad...