Soy-based adhesives have attracted much attention recently because they are environmentally safe, low cost, and readily available. To improve the gluability and water resistance of soy-based adhesives, we prepared an enzyme-treated soy-based adhesive modified with an epoxy resin. We investigated the wet shear strength of plywood bonded with the modified adhesive using the boiling-water test. Fo...

Abstract There is increasing interests in the significant improvement of impregnation amount and efficiency wood by pre-treatment compression. Thus, attention paid to compression for harder with resin because large viscosity relatively molecular weight resin. Low-molecular-weight phenol formaldehyde (PF) solid content 10–48% were impregnated at a ratio 60% 40% poplar Chinese fir, respectively, ...

Experimental data are reported on moisture diffusion and the elastoplastic response in uniaxial tensile tests of an intercalated nanocomposite with vinyl ester resin matrix and montmorillonite clay filler at room temperature. Observations in diffusion tests show that the moisture transport in the neat resin is Fickian, whereas it becomes noticeably anomalous (non-Fickian) with the growth of the...

ber af problems fer nnr instantaneously While solvent-assisted emulsion systems have met with a degree of success in formulating pressure sensitive adhesives, they have several disadvantages. The solvent content of these systems precludes totally solvent-free adhesives. Also. there is reported evidence that surfactants used to stabilize the emulsion can adversely affect tack properties of the f...

A lignin-epoxy resin composite was prepared by blending lignin/wood flour with an epoxy resin and polyamine. The effects of the wood flour on the mechanical, thermal creep, and creep recovery properties, as well as the microstructure of the composite, were studied. Among the mechanical properties, the initial modulus increased with increasing content of wood flour. The glass transition temperat...

The aim of this study was to examine the mechanical properties of a new surface-modified denture resin for its suitability as denture base material. This experimental resin is made by copolymerization of methacrylic acid (MA) to poly(methyl methacrylate) (PMMA) to produce a negative charge. Four experimental groups consisted of Orthodontic Dental Resin (DENTSPLY Caulk) as a control and three gr...

The objective of this study was to investigate the effects of hot water extraction process on the dimensional stability of oriented strand composites. Aspen wood strands were extracted using various severity factor levels. Phenol formaldehyde and polymethylene diphenyl diisocyanate resins were used for production of the oriented strandboard panels. Six panel groups were produced from the extrac...