long–term stability and oxidation resistance of aisi 439 ferritic stainless steel used as interconnects in solid oxide fuel cells can be improved by use of a protective coating. in this study the pack cementation method was employed to coat aisi 439 ferritic stainless steel with manganese. isothermal oxidation was conducted at 800 ºc for 200 hours in static air to investigate the role of coatin...

The very thin native oxide film on stainless steel, of the order of 2 nm, is known to be readily modified by immersion in aqueous media. In this paper, XPS and ToF-SIMS are employed to investigate the nature of the air-formed film and modification after water emmersion. The film is described in terms of oxide, hydroxide and water content. The preferential dissolution of iron is shown to occur o...

protective coatings that resist oxide scale growth and decrease chromium evaporation are necessary to makestainless steel interconnect materials for long-term durable operation of solid oxide fuel cells (sofcs). inthis study a layer of manganese was coated on the surface of aisi 441 ferritic stainless steel which is used insolid oxide fuel cells for interconnect applications. the oxidation beha...

The feasibility and parameters optimization of AA5183 aluminum cladding on AISI 1018 steel by electro spark microwelding (ESM) and the corrosion resistance of the clad plate were investigated. The optimum conditions were found as 15 A, 10%, 800 Hz and 2500 rpm for P, D, F and R factors, respectively. Confirmation test under optimum conditions showed that the model can be effectively used to pre...

The subsystem Nurse’s A-phase-silicocarnotite within the system Ca3(PO4)2–Ca2SiO4 was conducted as a preliminary step toward obtaining new biomaterials with controlled microstructures. Phase composition of the resulting ceramics was studied by X-ray diffraction, differential thermal analysis, and scanning electron microscopy with attached wavelength dispersive spectroscopy. The results showed t...