Nanostructured bainite was obtained in high-carbon Si-Al-rich steel by low-temperature (220-260 °C) isothermal transformation after austenitisation at different temperatures (900 °C, 1000 °C, and 1150 °C). Improved strength-ductility-toughness balance was achieved in the nanostructured bainitic steel austenitised at low temperatures (900 °C and 1000 °C). Increasing the austenitising temperature...

Depending on the starting equilibrium temperature, the application of a magnetic field on a sample of Ni–Mn–Sn produces sample heating or cooling during adiabatic experiments. The competition between endothermal and exothermal effects is observed close to the martensite-to-austenite magnetostructural phase transition. A model assuming the coexistence of two phases and a field dependence of thei...

The effects of carbon content on the dynamic and static softening mechanisms of Ti microalloy steels were investigated both in ferrite and austenite regions. &#10The results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. This is due to the Ti(CN) and TiC precipitates and also the free carbon content. In the ferrite r...

The microstructure of 8 mm diameter wire produced by the severe deformation of 316L austenitic stainless steel has been examined using TEM and X-ray diffraction. The deformation imparted amounts to a true strain of 6.3. Data from previous studies on strain induced transformation of this steel have been combined with new results to show that true strains .2 are required in order to observe mecha...

The effects of carbon content on the dynamic and static softening mechanisms of Ti microalloy steels were investigated both in ferrite and austenite regions. The results obtained showed that recrystallization rate decreased as the percentage of carbon content was increased from 0.0035 to 0.110. This is due to the Ti(CN) and TiC precipitates and also the free carbon content. In the ferrite reg...

Susceptibility of three lean-alloyed ferritic-austenitic stainless steels to hydrogen-induced delayed cracking was examined, concentrating on internal hydrogen contained in the materials after production operations. The aim was to study the role of strain-induced austenite to martensite transformation in the delayed cracking susceptibility. According to the conducted deep drawing tests and cons...

the development of nano/ultrafine bainitic structure in aisi 52100 steel was the goal of this study. for this purpose,the aisi 52100 the specimens were austenitized at 1050 °c for 60 min followed by low-temperature austemperingtreatment at different temperatures and times. the austempered samples were characterized using field emissionscanning electron microscopy (fesem), x-ray diffraction (xrd...

INTRODUCTION To improve the fracture resistance of nickel-titanium (NiTi) files, manufacturers have introduced new alloys and developed new manufacturing processes for the fabrication of NiTi files. This study aimed to examine the phase transformation behavior and microstructure of NiTi instruments from a novel controlled memory NiTi wire (CM wire). METHODS Instruments of EndoSequence (ES), P...

The microstructure and mechanical properties of Zr48Cu48 - x Al4M x (M ≡ Fe or Co, x = 0, 0.5, 1 at.%) metallic glass (MG) composites are highly dependent on the amount of Fe or Co added as microalloying elements in the parent Zr48Cu48Al4 material. Addition of Fe and Co promotes the transformation from austenite to martensite during the course of nanoindentation or compression experiments, resu...

The work reports an experimental observation on crystal rotation in a duplex (austenite + ferrite) steel induced by the electropulsing treatment at ambient temperature, while the temperature rising due to ohmic heating in the treatment was negligible. The results demonstrate that electric current pulses are able to dissolve the initial material's texture that has been formed in prior thermomech...