Plasma and halogen lamp units were used to photo-cure a composite resin for porcelain bonding. Mean shear bond strengths to dentin after light curing through porcelain of 1 and 2 mm thickness ranged from 20 to 27 MPa before and after thermocycling, indicating no significant effects due to porcelain thickness, curing method, or thermocycling, except for plasma curing for 3 s through porcelain of...

Aim To evaluate the fracture resistance of simulated immature teeth with an apical plug of biodentine followed by composite resin vs total obturation with biodentine tested immediately and after 3 months of aging and also to find out the chemical composition of dentin in contact with these materials. Materials and methods Extracted human maxillary central incisors with simulated immature apex...

PURPOSE There have been anecdotal reports of low bond strength with autocured resin composite materials, particularly when light-cured bonding agents that combine primer and adhesive in a 1-bottle preparation are used. The objective of this study was to determine if the mode of polymerization of the bonding agent influences the strength of the attachment of autocured resin composite luting ceme...

Objectives: To compare two different dual-curing resins cement interfaces between low translucency and high translucency lithium disilicate glass-ceramics in vitro. M~aterials and Methods: ISO 11405 was modeled by using a standardized dumb-bell test to compare the tensile bond strength of two different resin cement interfaces ofa low translucency lithium disilicate ceramic to a high translucenc...

OBJECTIVES To evaluate the microtensile bond strength (microTBS) of one- (Xeno III, Dentsply) and two-step (Tyrian-One Step Plus, Bisco) self-etching adhesive systems bonded to dentin and cemented to chemically cured (C&B Metabond) or light-cured paste of a dual-cure resin cement (Variolink II, Ivoclar) within a short (24 h) and long period of evaluation (90 days). MATERIAL AND METHODS Forty ...

PURPOSE Among the surface treatment methods suggested to enhance the adhesion of resin cement to fiber-reinforced composite posts, conflicting results have been obtained with silanization. In this study, the effects of silanization, heat activation after silanization, on the bond strength between fiber-reinforced composite post and resin cement were determined. MATERIALS AND METHODS Six group...

BACKGROUND The heat produced by provisional restoration materials may injure the dental pulp. This study measured and compared peak temperatures during polymerization of 5 materials used in the fabrication of provisional restorations. METHODS The tested materials were 2 self-curing resins (Integrity and Protemp) and 3 dual-cure resins (Iso-Temp, TCB Dual Cure and Provipont DC). A mould the si...

INTRODUCTION CAD/CAM (computer-aided design and computer-aided manufacturing) systems have refreshed the idea of chair-side production of restorations, but the fracture of ceramic veneers remains a problem. Cementation with glass fibers may improve the fracture strengths and affect the failure modes of CAD/CAM-generated ceramic veneers. Therefore, this study compared the fracture strengths of c...

OBJECTIVE The aim of this study was to assess the bond strength of indirect composite restorations cemented with a resin-based cement associated with etch-and-rinse and self-etching primer adhesive systems to dentin treated or not with a bioactive material. MATERIALS AND METHOD Twenty bovine incisor crowns had the buccal enamel removed and the dentin ground flat. The teeth were assigned to 4 ...